D04 - Road and Paving Materials

SIGNIFICANCE AND USE
5.1 The kinematic viscosity characterizes flow behavior. The method is used to determine the consistency of liquid asphalt as one element in establishing the uniformity of shipments or sources of supply. The specifications are usually at temperatures of 60 and 135 °C.
Note 3: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers procedures for the determination of kinematic viscosity of liquid asphalts, road oils, and distillation residues of liquid asphalts all at 60 °C [140 °F] and of liquid asphalt binders at 135 °C [275 °F] (see table notes, 11.1) in the range from 6 to 100 000 mm2/s [cSt].  
1.2 Results of this test method can be used to calculate viscosity when the density of the test material at the test temperature is known or can be determined. See Annex A1 for the method of calculation.  
Note 1: This test method is suitable for use at other temperatures and at lower kinematic viscosities, but the precision is based on determinations on liquid asphalts and road oils at 60 °C [140 °F] and on asphalt binders at 135 °C [275 °F] only in the viscosity range from 30 to 6000 mm2/s [cSt].
Note 2: Modified asphalt binders or asphalt binders that have been conditioned or recovered are typically non-Newtonian under the conditions of this test. The viscosity determined from this method is under the assumption that asphalt binders behave as Newtonian fluids under the conditions of this test. When the flow is non-Newtonian in a capillary tube, the shear rate determined by this method may be invalid. The presence of non-Newtonian behavior for the test conditions can be verified by measuring the viscosity with viscometers having different-sized capillary tubes. The defined precision limits in 11.1 may not be applicable to non-Newtonian asphalt binders.  
1.3 Warning—Mercury has been designated by the United States Environmental Protection Agency (EPA) and many state agencies as a hazardous material that can cause central nervous system, kidney, and liver damage. Mercury, or its vapor, may be hazardous to health and corrosive to materials. Caution should be taken when handling mercury and mercury-containing products. See the applicable product Material Safety Data Sheet (MSDS) or Safety Data Sheet (SDS) for details and the EPA’s website—http://www.epa.gov/mercury/faq.htm—for additional information. Users should be aware that selling mercury, mercury-containing products, or both, in your state may be prohibited by state law.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.5 The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior ...

SIGNIFICANCE AND USE
4.1 This test method is useful in confirming that an asphalt cement has been modified with a material that provides a significant elastomeric component. Elastomer-modified asphalts can be characterized by their ability to be stretched to a large elongation while at the same time resisting further stretching. Toughness and tenacity are two parameters for measuring this ability.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method describes the procedure for measuring the toughness and tenacity of asphalt materials. Typically, the test method has been used to characterize elastomer-modified asphalts, although values for toughness and tenacity may be obtained for any type of polymer-modified or non-modified asphalt.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.2.1 Exception—Sample mass is given only in SI units. Sample mass as given in SI units should be regarded as standard. No other units of sample mass are included in this standard.  
1.3 Warning—Mercury has been designated by the United States Environmental Protection Agency and many state agencies as a hazardous material that can cause central nervous system, kidney, and liver damage. Mercury, or its vapor, may be hazardous to health and corrosive to materials. Caution should be taken when handling mercury and mercury-containing products. See the applicable Material Safety Data Sheet (MSDS) for details and EPA’s website—http://www.epa.gov/mercury/index.htm—for additional information. Users should be aware that selling mercury and/or mercury-containing products in your state may be prohibited by state law.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This procedure measures the amount of the more volatile constituents in cutback asphalt. The properties of the residue after distillation are not necessarily characteristic of the asphalt used in the original mixture, nor of the residue which may be left at any particular time after field application of the cutback asphalt. The presence of silicone in the cutback asphalt may affect the distillation residue by retarding the loss of volatile material after the residue has been poured into the residue container.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers a distillation test for cutback asphalts.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the standards for graded Trinidad Lake modified asphalt binders. Grading is related to the average seven-day maximum pavement design temperature, the intermediate pavement design temperature, and the minimum pavement design temperature. The Trinidad Lake modified asphalt binder shall be prepared by adding the Trinidad Lake asphalt modifier to base asphalt produced from the refining of petroleum crude. The base asphalt binder shall be homogenous, and free from water or any deleterious materials.
SCOPE
1.1 This specification covers performance-graded Trinidad Lake modified asphalt binders. Grading designations are related to the LTPPBind Online calculated maximum pavement design temperature and the minimum pavement design temperature.
Note 1: For more information on LTPPBind Online, see https://infopave.fhwa.dot.gov/Tools/LTPPBindOnline accessed July 10, 2023.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 The complex shear modulus is an indicator of the stiffness or resistance of asphalt binder to deformation under load. The phase angle is a measure of the relative portion of the response to an applied load that is elastic (recoverable) or viscous (nonrecoverable).  
5.2 The test procedure is applicable to measurements in the linear region where the measured modulus and phase angle are independent of the amplitude of the strain.  
5.3 The complex modulus and the phase angle are used to calculate performance-related criteria in accordance with Specification D6373 or D8239.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the determination of the complex shear modulus and phase angle of asphalt binders when tested in dynamic (oscillatory) shear using parallel plate geometry.  
1.2 This test method is intended for determining the linear viscoelastic properties of asphalt binders as required for specification testing and is not intended as a comprehensive procedure for the full characterization of the viscoelastic properties of asphalt binder.  
1.3 This standard is appropriate for unaged asphalt binder, conditioned asphalt binder, and asphalt binder recovered from either asphalt mixtures or asphalt emulsions. To keep the language in this standard precise, the term “asphalt binder” is used to refer to the material being tested.  
1.4 This procedure is limited to asphalt binders that contain particles with largest dimension less than 250 μm.  
1.5 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.6 Warning—Mercury has been designated by the United States Environmental Protection Agency (EPA) and many state agencies as a hazardous material that can cause central nervous system, kidney, and liver damage. Mercury, or its vapor, may be hazardous to health and corrosive to materials. Caution should be taken when handling mercury and mercury-containing products. See the applicable product Safety Data Sheet (SDS) for details and EPA’s website— www.epa.gov/mercury/faq.htm—for additional information. Users should be aware that selling mercury, mercury-containing products, or both, into your state may be prohibited by state law.  
1.7 This standard may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 This test is primarily used for field production control of asphalt-rubber (A-R) and other high-viscosity binders; however, the test can also be used in a laboratory setting.  
3.2 A handheld rotational viscometer is used to measure the apparent viscosity of a completed blend of A-R or high-viscosity binder. A rotor (spindle), turning at constant speed, is inserted in the liquid binder to be measured. The resistance to movement of the spindle (torque) caused by the viscosity of the surrounding liquid is measured using a special mechanism to obtain direct readings in Pa·s or cP.
Note 1: Spindle is generally made of stainless steel, although another metal such as brass could be used.  
3.3 The measured apparent viscosity is used to control the production of the A-R or other high-viscosity binder, to assess the uniformity of the binder produced, or for other related purposes.  
3.4 As the spindle turns in the A-R or other high-viscosity binder, it has a tendency to “drill” into the sample (that is, for A-R, the spindle spins the rubber particles out of the measurement area). Consequently, the apparent viscosity drops to reflect only the liquid phase of the high-viscosity binder. Therefore, the peak viscosity measurement value is recorded to reflect the viscosity of the blended material.
SCOPE
1.1 The use of high-viscosity asphalt binders like asphalt-rubber is becoming more common in the United States and worldwide. Specifications such as Specification D6114/D6114M note the need for field control of the apparent viscosity and require the use of a field production rotational viscometer. The testing of asphalt-rubber binder for use in asphalt-rubber hot mix and for asphalt-rubber membrane is necessary to ensure consistent mix properties that will ensure good performance of these materials. Logistics of field applications limits the use of conventional laboratory controls and testing equipment. This test, using a handheld rotational viscometer, can be conducted in either the field or laboratory to determine the apparent viscosity of asphalt-rubber and other high-viscosity binders for field production control and to assess the uniformity of the binder produced, or for other related purposes.  
1.2 Asphalt-rubber binder consists of a blend of paving grade asphalt cement and crumb rubber as described in Specification D6114/D6114M. Other high-viscosity asphalt binders may consist of asphalts modified with polymer or fiber, or both. Testing is performed following the specified reaction time, if any, within the production process. Control of the raw materials is separate from the test.  
1.3 The values stated in SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; each system shall be used independently of the other. Combining values from the two systems may result in noncompliance with the standard.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification covers preformed expansion joint filler having relatively little extrusion and substantial recovery after release from compression.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
Note 1: Attention is called to Specifications D1752 and D994/D994M.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 Workability is one of the main factors that influence the compaction quality and ultimately the performance of asphalt pavement. This method uses the relative rotation measured by the wireless particle-size sensor to evaluate the workability of the asphalt mixture.  
5.2 This test method is used to generate information concerning the workability of an asphalt mixture. Workability characteristics, in turn, can give users insight as to how the mixture will handle and compact in the field.  
5.3 This method is used to evaluate workability of the mix in a situation where it is being used for research or mix design. It is not intended to be a quality control (QC) evaluation.  
5.4 This test method can be used to evaluate conventional and modified asphalt mixtures to achieve the best workability at an appropriate compaction temperature. The test method can be used to determine the compaction temperature and optimal dosage rate of additives or modifiers to achieve the best workability for the modified asphalt mixtures, such as polymer modified, crumb rubber modified, waste plastic modified, etc.  
5.5 This test method is appropriate for laboratory-produced mixtures and plant-produced mixtures, regardless of the type or grade of the binder, the type or gradation of the aggregates, and whether RAP, WMA additives, or other modifiers are used in the asphalt mixture.
Note 1: The quality of the results produced by this standard is dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline...
SCOPE
1.1 This test method covers the determination of relative rotation to evaluate the workability of asphalt mixture during compaction using a wireless particle-size sensor. It is applicable to asphalt mixture being compacted using the Superpave Gyratory Compactor (SGC).  
1.2 This test method is appropriate for use to determine the relative rotation of laboratory-produced and plant-produced asphalt mixtures, regardless of the type or gradation of the aggregates, and whether reclaimed asphalt pavement (RAP), warm mix asphalt (WMA) additives, or any type of modifiers are used in the asphalt mixture.  
1.3 Units—The values stated in SI units are to be regarded as the standard. No other units of measurement are included in this standard.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered requirements of the standard.  
1.5 Since a complete precision and bias statement for this standard has not been developed, the test method is to be used for research and informational purposes only. Therefore, this standard should not be used for acceptance or rejection of a material for purchasing purposes.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers extended life type, nonplowable, retroreflective raised pavement markers for nighttime lane marking and delineation. Pavement markers shall undergo tests to examine their conformance with specified construction, performance (retroreflectivity), and physical property (flexural strength, compressive strength, abrasion resistance, coefficient of luminous intensity, color, resistance to lens cracking, lens impact strength, and temperature cycling strength) requirements.
SCOPE
1.1 This specification covers nonplowable, retroreflective raised pavement markers for nighttime lane marking and delineation.  
1.2 The values stated in inch-pound units are to be regarded as the standard, except where noted in the document. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following precautionary caveat pertains only to the test methods portion, Section 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 The compression resistance perpendicular to the faces, the resistance to the extrusion during compression, and the ability to recover after release of the load are indicative of a joint filler's ability to continuously fill a concrete expansion joint and thereby prevent damage that might otherwise occur during thermal expansion. The asphalt content is a measure of the fiber-type joint filler's durability and life expectancy. In the case of cork-type fillers, the resistance to water absorption and resistance to boiling hydrochloric acid are relative measures of durability and life expectancy.
Note 2: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 These test methods cover the physical properties associated with preformed expansion joint fillers. The test methods include:    
Property  
Section  
Expansion in Boiling Water  
7.1  
Recovery and Compression  
7.2  
Extrusion  
7.3  
Boiling in Hydrochloric Acid  
7.4  
Asphalt Content  
7.5  
Water Absorption  
7.6  
Density  
7.7
Note 1: Specific test methods are applicable only to certain types of joint fillers, as stated herein.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This practice simulates the polishing action of vehicular traffic on coarse aggregates used in bituminous pavements.  
4.2 A polish value is determined that may be used to rate or classify coarse aggregates for their ability to resist polishing under traffic.
Note 1: The quality of the results produced by this standard are dependant upon the competence of the personnel performing the procedure and the capability, calibration, and the maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors: following the suggestions of Specification D3666 or similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This practice covers a laboratory procedure by which an estimate may be made of the extent to which different coarse aggregates may polish.  
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. Regarding sieves, per Specification E11: “The values stated in SI units shall be considered standard for the dimensions of the wire cloth openings and the diameter of the wires used in the wire cloth.” When sieve mesh sizes are referenced, the alternate inch-pound designations are provided for information purposes and enclosed in parentheses.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers asphalt plank used for bridge decks as well as for industrial floors. Asphalt planks shall be classified according to usage: Type Ia; Type Ib; and Type II. Asphalt plank shall be formed from a mixture of asphalt, fibers, modifiers, or a combination thereof, and mineral filler in such a manner as to produce a uniformly dense mass. The following test methods shall be intended to measure those attributes necessary to measure the ability of asphalt plank to provide a reasonably long and satisfactory service: absorption; brittleness; dimensions; and hardness.
SCOPE
1.1 This specification covers asphalt plank used for bridge decks as well as for industrial floors.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 The float test characterizes the flow behavior or consistency of certain asphalt materials.  
4.2 This test method is useful in determining the consistency of asphalt as one element in establishing the uniformity of certain shipments or sources of supply.
Note 1: The quality of results produced by this standard is dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guidance provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the float test for asphalt materials.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 Warning—Mercury has been designated by EPA and many state agencies as a hazardous material that can cause central nervous system, kidney, and liver damage. Mercury, or its vapor, may be hazardous to health and corrosive to materials. Caution should be taken when handling mercury and mercury-containing products. See the applicable product Material Safety Data Sheet (MSDS) for details and EPA’s website (http://www.epa.gov/mercury/faq.htm) for additional information. Users should be aware that selling mercury or mercury-containing products, or both, in your state may be prohibited by state law.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 The procedure described in this practice is used to design and construct an asphalt-rubber cape seal that will provide a wearing course when subjected to low to medium traffic volumes and where the pavement distress is due to block-type cracking resulting from pavement aging or reflective cracking only (not where there are clear indications of fatigue cracking due to repeated heavy axle loads).
Note 2: Block cracking is defined in Practice D6433. See Appendix X1 for an example of block cracking due to aging.
SCOPE
1.1 This practice covers asphalt-rubber cape seal, which is defined as the application of an asphalt-rubber seal coat placed onto an existing pavement surface, followed by the application of a conventional Type II or III slurry seal.
Note 1: An asphalt-rubber seal coat is also known as a stress absorbing membrane (SAM), which consists of an asphalt-rubber membrane seal followed by the application of pre-coated aggregate chips.  
1.2 An asphalt-rubber cape seal is commonly used to extend the service life of low to medium trafficked and moderately distressed asphalt-surfaced pavements. The existing pavement condition can be used to determine the application rates for the asphalt-rubber binder and aggregate as well as the aggregate gradation. Pavements in relatively poor condition will require a coarser aggregate with a higher binder application rate.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 This test method can be used to determine whether the amount of draindown measured for a given asphalt mixture is within specified acceptable levels. The test provides an evaluation of the draindown potential of an asphalt mixture during mixture design and/or during field production. This test is primarily used for mixtures with high coarse aggregate content such as porous asphalt (open-graded friction course) and stone matrix asphalt (SMA).
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the determination of the amount of draindown in an uncompacted asphalt mixture sample when the sample is held at elevated temperatures comparable to those encountered during the production, storage, transport, and placement of the mixture. The test is particularly applicable to mixtures such as porous asphalt (open-graded friction course) and stone matrix asphalt (SMA).  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This practice is to be used as a guide and not a specification.
SCOPE
1.1 This practice covers the design and construction of asphalt surface treatments. It is a guide and should be used as such. End-use specifications should be adopted to conform to job and user requirements.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific precautions, see Section 9.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 Sampling is as important as testing, and precautions shall be taken to obtain samples to show the true nature and condition of the materials.  
4.2 Samples are taken for either of the following two purposes:  
4.2.1 To represent as nearly as possible an average of the bulk of the materials sampled, or  
4.2.2 To ascertain the maximum variation in characteristics which the material possesses.
SCOPE
1.1 This practice applies to the sampling of asphalt materials at points of manufacture, storage, or delivery.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 This test method is used to identify or classify an emulsified asphalt as an RS or MS by measuring the amount of available asphalt that is broken from the emulsified asphalt by utilizing specified amounts and concentrations of calcium chloride solution for anionic emulsified asphalts and dioctyl sodium sulfosuccinate for cationic emulsified asphalts.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method, applicable to both anionic and cationic emulsified asphalts of the RS and MS type, measures the chemical breaking of the emulsified asphalt.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification covers preformed expansion joint fillers made from closed-cell polypropylene foam materials having suitable compressibility, recovery from compression, nonextruding, and weather-resistant characteristics.  
1.1.1 Type I, closed-cell polypropylene foam.  
1.2 These joint fillers are intended for use in concrete pavements in full-depth joints. There are several variations in size with typical thicknesses of 1/2 in. (12.7 mm), 3/4 in. (19.05 mm), and 1 in. (25.4 mm); typical widths of 31/2 in. (88.9 mm), 4 in. (101.6 mm), 5 in. (127 mm), 6 in. (152.5 mm), 7 in. (177.8 mm), 8 in. (203.2 mm), or 48 in. (1.2 m) sheet; and typical lengths of 5 ft (1.52 m) and 10 ft (3.05 m).  
1.3 The values stated in inch-pound units are to be regarded as the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers asphalt-rubber binder, consisting of a blend of paving grade asphalt cements, ground recycled tire (that is, vulcanized) rubber and other additives, as needed, for use as binder in pavement construction. The rubber shall be blended and interacted in the hot asphalt cement sufficiently to cause swelling of the rubber particles prior to use. Tests shall be performed to conform with the physical requirements of the asphalt-rubber binder, in accordance with the following test methods: apparent viscosity; modified test method; penetration; softening point; resilience; flash point; thin-film oven test residue; and penetration retention.
SCOPE
1.1 This specification covers asphalt-rubber binder consisting of a blend of asphalt binder, ground recycled tire (that is, vulcanized) rubber, and other additives, as needed, for use as binder in pavement construction. The rubber shall be blended and interacted in the hot asphalt binder sufficiently to cause swelling of the rubber particles prior to use.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 Since a precision estimate for this standard has not been developed, the test method is to be used for research and informational purposes only. Therefore, this standard should not be used for acceptance or rejection of a material for purchasing purposes.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.  
1.5 The following precautionary caveat pertains to the test method portions only, Sections 4 and 5 of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in 4.3.2.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This test method is used to prepare specimens for determining the volumetric and physical properties of compacted asphalt mix.  
4.2 This test method is useful for monitoring the density of test specimens during the compaction process. This test method is suited for the laboratory design, field control of asphalt mix, forensics, imaging, and visualization of compacted asphalt mix.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the compaction of an asphalt mix into cylindrical specimens using the Superpave Gyratory Compactor (SGC). This standard also refers to the determination of the relative density of the compacted specimens at any point in the compaction process. Compacted specimens are suitable for volumetric, physical property, and mechanical testing. Smaller specimens may be cut from the compacted cylindrical specimen for specific test specimen geometry requirements. The compaction procedures apply to Laboratory Mixed Laboratory Compacted (LMLC) and Plant Mixed Laboratory Compacted (PMLC) asphalt mix.  
1.2 The values stated in SI units are to be regarded as standard. The values given in degrees for the angle of gyration, gyrations per minute, and hardness are mathematical conversions from the SI units and are provided for information regarding the commonly used units of degree, rotations per minute, and Rockwell hardness, respectfully.  
1.3 The text of this test method references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This performance specification covers mixtures of water-based latex polymer, mineral aggregates, and optional other admixtures that, when combined, create a weather-protective and aliphatic hydrocarbon-resistant coating over asphalt and other pavements. There are two variations of the coating (Class 1 and Class 2): Class 1, a standard version—typically black but can be other colors, and Class 2, designed to be a solar reflective version.  
1.2 Units—The values stated in SI units are to be regarded as the standard. No other units of measurement are included in this standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements for the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 The maximum specific gravities and densities of asphalt mixtures are intrinsic properties whose values are influenced by the composition of the mixture in terms of types and amounts of aggregates and asphalt materials.  
5.1.1 They are used to calculate values for percent air voids in compacted asphalt mixtures.  
5.1.2 They provide target values for the compaction of asphalt mixtures.  
5.1.3 They are essential when calculating the amount of asphalt binder absorbed by the internal porosity of the individual aggregate particles in an asphalt mixture.
Note 2: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the determination of maximum specific gravity and density of uncompacted asphalt mixtures at 25 °C [77 °F].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This guide provides guidance as to the appropriate/typical mineralogy observed when iron and steel slag is produced during a variety of processes in the manufacture of iron and steel.  
4.2 Slag can be considered a product based on the mineralogy of samples that are tested using X-ray diffraction, phase recognition and characterization, powdered XRD-Rietveld analysis, and SEM-PARC results, using this guide.
SCOPE
1.1 This standard is intended to provide guidance as to the appropriate/typical mineralogy observed when iron and steel slag, produced during the manufacture of iron and steel, is designated as a product. The included information covers the mineral properties of blast furnace slag and steel slag when they are manufactured in conjunction with the production of iron or steel, or both (Note 1).  
Note 1: This guide is not intended to be used to determine the applicability of iron or steel slag, or both, for various applications. Terminology D8 designates steel slag as a product, while Terminology C125 designates blast furnace slag as a product. Its sole intent is to provide guidance as to the typical mineralogy when the iron or steel slag, or both, is designated as a product.  
1.2 The values stated in SI units are to be regarded as standard. No other units are utilized in this standard.  
1.3 The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) should not be considered as requirements of the specification.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 The particle shape of coarse aggregates influences the properties of some construction materials and may affect their placement and consolidation.  
5.2 This test method provides a means for checking compliance with specifications that limit such particles or to determine the relative shape characteristics of coarse aggregates.
SCOPE
1.1 This test method covers the determination of the percentages of flat particles, elongated particles, or flat and elongated particles in coarse aggregates. Two procedures, Method A and Method B, are presented in this standard. Method A is a reflection of the original procedure as developed prior to Superpave and is intended for all non-Superpave applications. Method B is a comparison of the maximum particle dimension to the minimum particle dimension and is intended for use with Superpave specifications.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.2.1 Exception (regarding sieves, per Specification E11)—The values stated in SI units shall be considered standard for the dimensions of the wire cloth openings and the diameter of the wires used in the wire cloth. When sieve mesh sizes are referenced, the alternate inch-pound designations are provided for information purposes and enclosed in parentheses.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the daytime and nighttime color of retroreflective pavement marking materials, both painted and tape lines, including thermoplastic, epoxy and other types, used for traffic control lane markings and symbols on road surfaces. This specification is not applicable to the testing, for quality control purposes, of marking material without added drop-on beads. The performance requirements for which the marking materials shall be tested on and conform accordingly to are the daytime and nighttime chromaticity limits, retroreflectance, and daytime lightness limits (Y tristimulus coordinate).
SCOPE
1.1 This specification covers the daytime and nighttime color of retroreflective pavement marking materials used for traffic control lane markings and symbols on road surfaces.  
1.2 This specification applies to all retroreflective pavement markings (markings that include retroreflective optics residing on the surface) except structured pavement markings as defined in 3.2.5.  
1.3 This specification is not applicable to pavement markings that do not include retroreflective optics on the surface.  
1.4 This specification does not address any requirements other than the color of retroreflective pavement markings.  
1.5 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.5.1 Exception—This specification is noted to be an SI document, where angles are generally expressed in radians. However, as angles used in retroreflection have historically been identified in degrees, the International Committee for Weights and Measures (CIPM, Comité International des Poids et Mesures) accepts the use of degrees with SI units, and European Normatives and documents from the International Commission on Illumination (CIE) use degrees for retroreflection geometry.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 The results obtained from this method can be used to determine the unit weight of compacted asphalt mixtures, and in conjunction with Test Method D3203/D3203M, to obtain percent air voids. These values in turn may be used in determining the relative degree of compaction.  
4.2 Since specific gravity has no units, it must be converted to density in order to do calculations that require units. This conversion is made by multiplying the specific gravity at a given temperature by the density of water at the same temperature.  
4.3 This method can be used for 100 mm [4 in.] and 150 mm [6 in.] diameter cylindrical as well as cubical asphalt mixture specimens to correct for inconsistencies in sample weight determinations resulting from drainage of water from samples and inaccuracy in saturated surface dry weight of absorptive coarse and open-graded mixes. Asphalt mixes such as stone matrix asphalt (SMA), porous friction course, and coarse-graded mixes with significant surface texture and interconnected voids can be tested with this method. Follow manufacturer recommendation for appropriate bag sizes to be utilized with cubical and abnormally shaped samples.4
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the determination of bulk specific gravity of compacted asphalt mixtures by the vacuum sealing method.  
1.2 This method can be used for compacted cylindrical and cubical laboratory and field asphalt mixture specimens.  
1.3 The bulk specific gravity of the compacted asphalt mixtures may be used in calculating the unit weight of the mixture.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.5 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 Asphalt slabs compacted with the rolling compactor can be used to obtain specimens for further testing, including bulk specific gravity following Test Methods D1188/D1188M, D2726/D2726M, and D6752/D6752M, fatigue performance characteristics following Test Methods D7460 and D8237 or AASHTO T 321, and Hamburg wheel-track testing following AASHTO T 324.  
5.2 Specimens to perform other standard tests could also be obtained, as long as their volume is contained within the volume of a slab.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this practice are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline that provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This practice covers the fabrication of slabs of asphalt mix using an automated laboratory rolling compactor (RC). Compacted specimens are suitable for volumetric and physical property testing. This practice should not be used for acceptance or rejection of a material or for purchasing purposes.  
1.2 Units—The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers bearings, which consist of all elastomer or of alternate laminates of elastomer and steel, when the function of the bearings is to transfer loads or accommodate relative movement between a bridge superstructure and its supporting structure, or both. The bearings are furnished in four types as follows: plain elastomeric bearing pad; plain elastomeric sandwich bearing; steel-laminated elastomeric bearing; and steel-laminated elastomeric bearing with external load plate. The elastomer for the manufacture of the bearing is furnished in two types: Type CR and Type NR. The elastomer for the manufacture of the bearing is furnished in four grades of low-temperature properties: Grade 0; Grade 2; Grade 3; and Grade 5. The elastomeric compound used in the construction of a bearing shall contain only either natural rubber or chloroprene rubber as the raw polymer. Internal steel laminates shall be of rolled mild steel. Plain bearing pads shall be molded individually, or cut from previously molded strips or slabs, or extruded and cut to length. A steel-laminated bearing or a plain sandwich bearing shall be molded as a single unit under pressure and heat. All bonding of elastomer to steel laminates and to external load plates shall be carried out during molding. Bearing compression tests, compression stiffness, visual inspection, quality control properties, shear modulus, ozone resistance, and low-temperature grade tests shall be performed to conform to the specified requirements.
SCOPE
1.1 This specification covers bearings which consist of all elastomer or of alternate laminates of elastomer and steel, when the function of the bearings is to transfer loads or accommodate relative movement between a bridge superstructure and its supporting structure, or both.  
1.2 The values stated in SI units are to be regarded as the standard.  
Note 1: The words “elastomer” or “elastomeric” will be used interchangeably with the word “rubber” in this specification.  
1.3 The following safety hazards caveat pertains only to the test methods portion, Section 8, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 This test method measures the amount of water present in the emulsified asphalt, as distinguished from either bitumen or petroleum solvent.
SCOPE
1.1 These test methods and practices, given under the headings titled Composition, Consistency, Stability, and Examination of Residue, cover the examination of asphalt emulsions composed principally of a semisolid or liquid asphaltic base, water, and an emulsifying agent. The test methods cover the following tests and practices:    
Test  
Sections  
Composition:  
Water Content  
4 – 10  
Residue and Oil Distillate by Distillation  
See Test Method
D6997  
Residue by Evaporation  
See Test Method
D6934  
Particle Charge of Cationic Emulsified Asphalts  
See Practice
D7402  
Consistency:  
Viscosity (Saybolt Furol)  
See Test Method
D7496  
Stability:  
Demulsibility  
See Test Method
D6936  
Settlement  
See Test Method
D6930  
Cement Mixing  
See Test Method
D6935  
Sieve Test  
See Test Method
D6933  
Aggregate Coating  
See Practice
D6998  
Miscibility with Water  
See Practice
D6999  
Freezing  
See Practice
D6929  
Coating Ability and Water Resistance  
11 – 18  
Storage Stability of Asphalt Emulsion  
See Test Method
D6930  
Examination of Residue  
19 – 26  
Identification Test for Rapid Setting Cationic Emulsified Asphalt  
27 – 34  
Identification of Cationic Slow Set Emulsions  
See Practice
D7402  
Field Coating Test on Emulsified Asphalts  
35 – 40  
Emulsified Asphalt/Job Aggregate Coating Test  
41 – 46  
Density of Emulsified Asphalt  
See Test Method
D6937  
Residue by Low-Temperature Vacuum Distillation  
See Test Method
D7403  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This test method for measuring the electrical resistivity of water-barrier membrane-pavement systems may be interpreted to indicate the effectiveness of such systems.  
4.2 This test method is predicated on the fact that an electrical connection between the surface of the pavement and the reinforcing steel in the concrete pavement cannot be made through an impermeable water-barrier membrane.  
4.3 This test method may be used for acceptance when the accepting agency specifies the minimum resistance value desired.  
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the measurement of the electrical resistivity of water-barrier membrane-pavement systems when applied to concrete bridge decks.  
1.2 Measurements shall be performed on the bituminous pavement surface covering the water-barrier membrane.  
1.3 This test method utilizes a measure of electrical resistance between the saturated top surface of the water-barrier membrane and the reinforcing steel embedded in the concrete bridge deck.  
1.4 The values measured represent the electrical resistance obtained with the equipment and procedures stated herein and do not necessarily agree or correlate with those using other equipment or procedures.  
1.5 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.6 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers asphalt binders graded by performance. Grading designations are related to the average seven-day maximum pavement design temperature, and minimum pavement design temperature. Asphalt binder shall be prepared by the refining of crude petroleum by suitable methods, with or without the addition of modifiers, which may be any organic material of suitable manufacture that is used in virgin or recycled condition, and that is dissolved, dispersed or reacted in asphalt cement to enhance its performance. This specification incorporates an aid for determining the critical low cracking temperature using a combination of test procedures.
SCOPE
1.1 This specification2 covers asphalt binders graded by performance. Grading designations are related to the LTPPBind Online calculated maximum pavement design temperature and the minimum pavement design temperature. This specification contains Tables 1 and 2. Table 2 incorporates Practice D6816 for determining the critical low cracking temperature using a combination of Test Method D6648 and Test Method D6723 test procedures. If no table is specified, the default is Table 1.
Note 1: For more information on LTPPBind Online, see https://infopave.fhwa.dot.gov/Tools/LTPPBindOnline accessed May 23, 2023.
Note 2: For asphalt cements graded by penetration at 25 °C, see Specification D946/D946M. For asphalt cements graded by viscosity at 60 °C, see Specification D3381/D3381M.
Note 3: AASHTO R 29 provides non-mandatory information for determining the performance grade of an asphalt binder.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification2 covers asphalt binders graded by performance. Grading designations are related to the LTPPBind Online calculated maximum pavement design temperature, the minimum pavement design temperature, and the traffic loading.
Note 1: For more information on LTPPBind Online, see https://infopave.fhwa.dot.gov/Tools/LTPPBindOnline accessed May 23, 2023.  
1.2 This specification incorporates Test Method D7405 for determining non-recoverable creep compliance, Jnr. “S,” “H,” “V,” or “E” designations must be specified for standard, heavy, very heavy, and extremely heavy traffic loading, respectively.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.
Note 2: A guidance document for specifying bodies using R % for elastic properties is under development.
Note 3: For asphalt binders graded by penetration at 25 °C, see Specification D946/D946M. For asphalt binders graded by viscosity at 60 °C, see Specification D3381/D3381M. For performance-graded asphalt binder, see Specification D6373.
Note 4: AASHTO R 29 provides non-mandatory information for determining the performance grade of an asphalt binder.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers preformed expansion joint fillers for use in concrete, brick, stone, and other paving and structural construction. The fillers are available in the following types: Type I, sponge rubber, which shall consist of preformed strips of a durable elastic sponge rubber compound using synthetic rubber or natural rubber as a base and containing no reclaim rubber or factice; Type II, cork, and Type III, self-expanding cork, which shall both consist of preformed strips that have been formed from clean granulated cork particles securely bound together by a synthetic resin of an incoluble nature; and Type IV, recycled PVC, which shall consist of preformed strips that have been extruded using scrap PVC material and using either no binder or a synthetic resin of an insoluble nature to securely bind it together. Materials shall be sampled suitably according to specified size and number, and shall meet property requirements as to recovery, compression, extrusion, expansion, boiling in hydrochloric acid, and density.
SCOPE
1.1 This specification covers preformed expansion joint fillers of the following four types for use in concrete, brick, or stone construction.  
1.1.1 Type I—Sponge rubber.  
1.1.2 Type II—Cork.  
1.1.3 Type III—Self-expanding cork.  
1.1.4 Type IV—Recycled PVC.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
Note 1: Attention is called to Specifications D994/D994M and D1751.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 Test Methods A and B provide percent void content determined under standardized conditions which depend on the particle shape and texture of a fine aggregate. An increase in void content by these procedures indicates greater angularity, less sphericity, rougher surface texture, or combinations thereof. A decrease in void content results is associated with more rounded, spherical, or smooth-surfaced fine aggregate, or a combination thereof.  
5.2 Test Method C measures the uncompacted void content of the minus 4.75 mm (No. 4) portion of the as-received material. This void content depends on grading as well as particle shape and texture.  
5.3 The void content determined on the standard graded sample (Test Method A) is not directly comparable with the average void content of the three individual size fractions from the same sample tested separately (Test Method B). A sample consisting of single-size particles will have a higher void content than a graded sample. Therefore, use either one method or the other as a comparative measure of shape and texture, and identify which test method has been used to obtain the reported data. Test Method C does not provide an indication of shape and texture directly if the grading from sample to sample changes.  
5.3.1 The standard graded sample (Test Method A) is most useful as a quick test which indicates the particle shape properties of a graded fine aggregate. Typically, the material used to make up the standard graded sample can be obtained from the remaining size fractions after performing a single sieve analysis of the fine aggregate.  
5.3.2 Obtaining and testing individual size fractions (Test Method B) are more time consuming and require a larger initial sample than using the graded sample. However, Test Method B provides additional information concerning the shape and texture characteristics of individual sizes.  
5.3.3 Testing samples in the as-received grading (Test Method C) may be useful in selecting proportio...
SCOPE
1.1 These test methods cover the determination of the loose, uncompacted void content of a sample of fine aggregate. When measured on any aggregate of a known grading, void content provides an indication of that aggregate's angularity, sphericity, and surface texture compared with other fine aggregates tested in the same grading. When void content is measured on an as-received fine-aggregate grading, it can be an indicator of the effect of the fine aggregate on the workability of a mixture in which it may be used.  
1.2 Three procedures are included for the measurement of void content. Two use graded fine aggregate (standard grading or as-received grading), and the other uses several individual size fractions for void content determinations:  
1.2.1 Standard Graded Sample (Test Method A)—This test method uses a standard fine aggregate grading that is obtained by combining individual sieve fractions from a typical fine aggregate sieve analysis. See the Section 9 for the grading.  
1.2.2 Individual Size Fractions (Test Method B)—This test method uses each of three fine aggregate size fractions: (a) 2.36 mm (No. 8) to 1.18 mm (No. 16); (b) 1.18 mm (No. 16) to 600 μm (No. 30); and (c) 600 μm (No. 30) to 300 μm (No. 50). For this test method, each size is tested separately.  
1.2.3 As-Received Grading (Test Method C)—This test method uses that portion of the fine aggregate finer than a 4.75 mm (No. 4) sieve.  
1.2.4 See the section on Significance and Use for guidance on the method to be used.  
1.3 The values stated in SI units shall be regarded as the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accor...

ABSTRACT
This specification establishes the material, manufacturing, and physical requirements for re-refined engine oil bottoms, also known as vacuum tower asphalt extender, that may be used in formulating asphalt for pavement construction and roofing. "Re-refined engine oil bottoms" (REOB) is the commonly used term used by many state highway agencies and FHWA, while "vacuum tower asphalt extender" (VTAE) is preferred by manufacturers. REOB/VTAE may be obtained by processing used engine oil using atmospheric distillation followed by vacuum distillation to produce a vacuum residuum meeting the requirements outlined in this specification. The REOB/VTAE shall be homogenous, free from water, and not foam when heated to 232°C (450°F).
SCOPE
1.1 This specification covers re-refined engine oil bottoms, also known as vacuum tower asphalt extender, that may be used in formulating asphalt for pavement construction and roofing. This specification has been developed specifically for these two categories of product and is not intended for other uses. Table 1 is to be used for pavement construction and Table 2 for roofing. “Re-refined engine oil bottoms” (REOB) is the prevailing name used by many state highway agencies and FHWA, while “vacuum tower asphalt extender” (VTAE) is the preferred name used by the manufacturers of the product. Since each name provides an important descriptor of production elements (“re-refined” and “vacuum tower”) for the specific product this specification addresses, this specification uses the term “REOB/VTAE.”  
1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This test is useful for classifying the curing and formulation of cold-mixed emulsified asphalt samples through ravel testing of compacted specimens. This performance test should be used to rank the mix conditions and approximate curing time for return to traffic and resistance to weather damage.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method measures the resistance to raveling characteristics of emulsified asphalt and field aggregates or recycled asphalt pavement (RAP) mixtures by simulating an abrasion similar to early return to traffic.  
1.2 A precision and bias statement for this standard has not been developed at this time. Therefore, this standard should not be used for acceptance or rejection of a material for purchasing purposes.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification covers flexible, retroreflective sheeting for use in high visibility markings to provide enhanced daytime and/or nighttime visibility for use on emergency response vehicles, utility vehicles, and similar vehicles.  
1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 The critical strain energy release rate parameter, Jc, is used to compare the cracking resistance of asphalt mixtures prepared with different asphalt binder and aggregate types prepared to meet the volumetric requirements of differing traffic levels tested at intermediate temperatures.  
5.2 The critical strain energy release rate parameter, Jc, is an engineering property and a performance indicator at intermediate temperature cracking.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the procedures for preparation, testing, and measurement of asphalt mixture cracking resistance at intermediate temperatures using semi-circular bend (SCB) geometry of laboratory-prepared or pavement core asphalt mixture samples tested monotonically. The SCB sample is a half-disk with a notch cut aligned vertically in parallel with the testing loading. The test method describes the determination of the critical strain energy release rate parameter, Jc, and other parameters determined from the load-displacement curve. These parameters can be used to rank the resistance of asphalt mixtures to cracking.  
1.2 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 Since a complete Precision and Bias statement for this standard has not been developed, the test method is to be used for research and informational purposes only. Therefore, this standard should not be used for acceptance or rejection of a material for purchasing purposes.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 This microsurfacing practice is written as a guide and should not be construed as a specification. End use specifications should be adapted to conform to job and user requirements.
Note 2: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This practice covers the design, testing, and construction of mixtures of polymer-modified asphalt emulsion, mineral aggregate, mineral filler, water, and other additives, properly proportioned, mixed and spread on a paved surface. It is written as a guide and should be used as such. End use specifications should be adapted to conform to job and user requirements.
Note 1: This practice references test methods outside the jurisdiction of ASTM that may or may not have a precision statement.  
1.2 The values stated in SI units are to be regarded as the standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This practice provides a guide for factors to be considered prior to waterproofing bridge decks with water barrier membrane systems. It will provide guidance for specification of materials, application of membrane systems, and placement of asphalt wearing courses. It may be used as a guide for new construction or for rehabilitation of existing structures.
SCOPE
1.1 This practice covers liquid applied, preformed, or built-up water barrier membrane systems and their application, overlaid with asphalt wearing courses, for use in the protection of bridge decks from deleterious effects of deicing salts. Material use and specifications should be adapted to conform to job and user requirements for new construction or existing structures. This practice is written as a guide for the use of bridge deck water barrier systems only.  
1.2 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in Section 10.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 Option A—The transverse and longitudinal application rate and variability in application rate of bituminous material applied to a pavement surface using a bituminous distributor can be estimated using Option A.  
3.2 Option B—The transverse and longitudinal residual application rate and variability in residual application rate from emulsified asphalt applications to a pavement surface using a bituminous distributor can be estimated by using Option B.
SCOPE
1.1 This practice covers the determination of transverse and longitudinal application rate and residual application rate of asphalt distributors in gallons per square yard (or litres per square metre).  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification covers bridge bearings that consist of an unconfined polyether urethane rotational element subjected to compression loads, along with a resisting mechanism to transmit shear and/or tension loads through the bearing. For expansion and/or contraction applications, an additional stainless steel flat surface slides against a carbon steel plate faced with sheet polytetrafluoroethylene (PTFE). The function of the bearing is to transfer loads and to accommodate any relative movement, including rotation between a bridge superstructure and its supporting structure, or both.  
1.2 The requirements stated in this specification are the minimums necessary for the manufacture of quality bearing devices. It may be necessary to increase these minimum values due to other design or construction conditions.  
1.3 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This standard specification covers a standardized method whereby an aromatic polyamide fiber can be evaluated prior to modification where the finished product (formulation of aramid fiber plus some form of treatment) is to be used in asphalt mixtures. The aromatic, polyamide fiber (shortened to “aramid” in non-treated form) can be specified by physical and mechanical properties whereby the aramid fiber is treated and the final product form is used in asphalt mixtures. The purpose of adding aramid fiber is to improve the asphalt mixture’s mechanical performance. Aramid fiber may provide structural properties to the mixture and thus is different than fibers such as cellulose fibers that are used to prevent drain down. The aramid fiber may be coated (that is, “treated”) with a binder such as wax, emulsion, or similar. The fiber can also be blended with a polyolefin fiber or other additive to reduce loss of fibers into the airstream during mixing due to the lightweight nature of aramid fiber. The mechanical properties listed in the standard specification are for the non-treated aramid fiber since it is difficult to test shortened fibers for properties such as linear density, tensile strength, and Young’s modulus.  
1.2 This standard specification does not address the performance of asphalt binder blends with aramid fiber or that of the asphalt mixture containing aramid fiber, but rather specifies the aramid fiber properties for use in formulating the finished product which is then used in asphalt mixtures.  
1.3 Units—The values stated in International System of Units (SI) are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers bridge bearings that consist of a spherical rotational element, where a stainless steel convex surface slides against a concave carbon steel plate covered with woven or sheet polytetrafluoroethylene (PTFE). The function of the bearing is to transfer loads and to accommodate any relative movement, including rotation between a bridge superstructure and its supporting structure, or both. The requirements of spherical bearings with a standard horizontal load (a maximum of 10 % of vertical) are discussed. The bearings are furnished in three types: fixed spherical bearing which is for rotation only, unidirectional sliding spherical bearing which is for rotation plus movement in one direction, and multi-directional sliding spherical bearing which is for rotation plus movement in all directions. The materials to be used in producing the bearings include: steel, stainless steel (flat sliding surface and convex surface), woven fabric polytetrafluoroethylene, and sheet polytetrafluoroethylene. The following different test methods shall be performed: proof load and rotation tests for fixed and expansion bearings, coefficient of friction test for expansion bearings only, PTFE (woven or sheet) bond test for expansion bearings only, and physical property test of both PTFEs for fixed and expansion bearings.
SCOPE
1.1 This specification covers bridge bearings that consist of a spherical rotational element, where a stainless steel convex surface slides against a concave carbon steel plate covered with woven or sheet polytetrafluoroethylene (PTFE). The function of the bearing is to transfer loads and to accommodate any relative movement, including rotation between a bridge superstructure and its supporting structure, or both.  
1.2 This specification covers the requirements of spherical bearings with a standard horizontal load (a maximum of 10 % of vertical).  
1.3 The requirements stated in this specification are the minima necessary for the manufacture of quality bearing devices. It may be necessary to increase these minimum values due to other design conditions.  
1.4 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.6 The following safety hazards caveat pertains only to the test method portion, Section 7, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
2.1 This practice may be used in conjunction with other methods in determining the general condition of concrete bridge decks.  
2.2 This practice may be used in determining specific areas of delamination requiring repair.
SCOPE
1.1 This practice covers procedures for surveying concrete bridge decks by sounding to determine delamination in the concrete. It is not intended that the procedures described herein are to be used on bridge decks that have been overlaid with asphalt mixtures. The procedures may be used on bridge decks that have been overlaid with portland cement concrete mixtures; however, areas indicated to be delaminated may have a lack of bond between the overlay and the underlying bridge deck (Note 1).  
Note 1: The influence of variable field conditions such as traffic noise, vibration, moisture content of the concrete, and the like, are not completely known and additional investigation may be needed. It is generally agreed that the practice should not be used on frozen concrete.  
1.2 The following three procedures are covered in this practice:  
1.2.1 Procedure A, Electro-Mechanical Sounding Device—This procedure uses an electric-powered tapping device, sonic receiver, and recorder mounted on a cart. The cart is pushed across the bridge deck and the delamination is recorded on the recorder.  
1.2.2 Procedure B, Chain Drag—This procedure consists of dragging a chain over the bridge deck surface. The detection of delamination is accomplished by the operator noting dull or hollow sounds. Tapping the bridge deck surface with a steel rod or hammer may be substituted for the chain drag.  
1.2.3 Procedure C, Rotary Percussion2—This procedure consists of rolling a dual-wheel, multi-toothed apparatus attached to an extension pole over the bridge deck surface. The percussive force caused by the tapping wheels will create either a dull or hollow sound, indicating any delamination.  
1.3 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.5 Since a complete Precision and Bias statement for this standard has not been developed, the standard practice is to be used for research and informational purposes only. Therefore, this standard should not be used for acceptance or rejection of a material for purchasing purposes.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers reflectorized thermoplastic based pavement striping material of the class that is applied to the road surface in a molten state by screed/extrusion or ribbon extrusion means. It deals with longitudinal applications in non snow plow areas, standard (non-profile) pavement marking applications, and applications on smooth asphalt or concrete surfaces. It does not include asphalt seal coat applications, which use large aggregate resulting in a very rough, open grade finish. This specification establishes requirements with respect to chemical composition and physical property of the thermoplastic pavement marking material, requirements for the optics that are used to reflectorize the thermoplastic pavement marking material after application, field performance requirements for the installed thermoplastic pavement markings, and material application requirements.
SCOPE
1.1 This specification covers a reflectorized thermoplastic-based pavement striping material of the class that is applied to the road surface in a molten state by screed/extrusion or ribbon extrusion means. Retroreflectivity of the pavement marking compound is achieved initially by surface application of retroreflective optics at the time of pavement marking application. Upon cooling to normal pavement temperature, the pavement marking material produces an adherent reflectorized stripe of specified thickness and width capable of resisting deformation by traffic. The pavement marking compound includes retroreflective optics (glass beads or composite optics, or both) that are incorporated into the material at the time of manufacture that provide retroreflective properties during the service life of the material.  
1.1.1 This specification is limited to:
1.1.1.1 Longitudinal applications in non snow plow areas,
1.1.1.2 Standard (non-profile) pavement marking applications, and
1.1.1.3 Applications on smooth asphalt or concrete surfaces. Asphalt seal coat applications, which use large aggregate resulting in a very rough, open grade finish, are excluded from this specification.  
1.1.2 This specification includes:
1.1.2.1 Compositional and physical property requirements of the thermoplastic pavement marking material,
1.1.2.2 Requirements for the optics that are used to reflectorize the thermoplastic pavement marking material after application,
1.1.2.3 Field performance requirements for the installed thermoplastic pavement markings, and
1.1.2.4 Material application requirements.  
1.2 The values stated in inch-pounds units are to be regarded as the standard except where noted in the document. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 The Micro-Deval abrasion test is a test of fine aggregate to determine abrasion loss in the presence of water and an abrasive charge. Many aggregates are more susceptible to abrasion when wet than dry, and the use of water in this test incorporates this reduction in resistance to degradation. The test results are helpful in evaluating the toughness/abrasion resistance of fine aggregate subject to abrasion when adequate information is not available from service records. This test is suitable for measuring the amount of weak, soft material such as shale or shaley carbonate in fine aggregate. Materials that give a low loss in this test are unlikely to exhibit significant degradation during handling, mixing, or placing. There is a relationship between drying shrinkage of cement mortar and Micro-Deval abrasion loss of fine aggregate, with higher loss materials resulting in higher drying shrinkage. Descriptions of the development of the test and the relationship with other properties have been published.3,4,5  
5.2 The Micro-Deval abrasion test on fine aggregate is useful for detecting changes in properties of aggregate produced from an aggregate source as part of a quality control or quality assurance process.  
5.3 The Micro-Deval abrasion test on fine aggregate, in contrast to the version on coarse aggregate, has a significant correlation with the magnesium sulfate soundness loss of fine aggregate. The Micro-Deval test on fine aggregate has better precision than the sulfate soundness test, is quicker, and may be used in place of that test. Advice on specific values for selection of aggregate will be found in the appendix.
SCOPE
1.1 This test method covers a procedure for testing fine aggregate for resistance to abrasion using the Micro-Deval apparatus.  
1.2 The text of this method references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the test method.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 Values of density are used for converting volumes to units of mass and for correcting measured volumes at the measured temperature to a standard temperature using Practice D4311/D4311M.
Note 2: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the determination of the relative density and density of semi-solid asphalt materials, asphalt binders, asphalt cements, and soft-tar pitches by use of a digital density meter (U-tube).
Note 1: Alternate methods for determining the density of semi-solid and solid asphalt materials and asphalt binders include Test Methods D3289, D3142/D3142M, and D70/D70M.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses are for information only. No other units of measurement are included in this standard, with the exception of temperature measurements. Units provided in degrees Fahrenheit are for reference purposes only. Temperatures given in degrees Celsius are to be considered standard.  
1.3 This test method should not be applied to petroleum distillates other than asphalt and asphalt binders. For the determination of density of all other petroleum distillates and viscous oils, use Test Method D4052 or D5002, or ISO 12185.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This guide covers the physical and chemical requirements of virgin or recovered foundry sand for use as a fine aggregate in asphalt mixtures.  
1.2 This guide is for use by contractors, foundry sand suppliers, or other purchasers as part of the purchase document describing the material to be furnished. Those responsible for selecting the proportions for the asphalt mixture should have the responsibility of determining the proportions of foundry sand as a fine aggregate.  
1.3 The values stated in SI units are to be regarded as the standard. No other units of measurement are included in this standard.  
1.4 The text of this standard references notes and footnotes which provide explanatory information. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of this standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.