B05.05 - Castings and Ingots for Remelting

ABSTRACT
This specification establishes requirements for continuously cast rod, bar, tube, and shapes produced from copper alloys with nominal compositions. Castings produced to this specification may be manufactured for and supplied from stock. Mechanical tests are required only when specified by the purchaser in the purchase order. Continuous castings shall not be mechanically repaired, plugged, or burned in. Weld repairs may be made at the manufacturer's discretion. For sampling purposes, a lot shall consist of castings of the same composition and same cross-sectional dimensions, produced during the continuous operation of one casting machine, and submitted for inspection at one time unless specified otherwise. The specimen shall be comprised of the following major elements: copper, tin, lead, zinc, iron, aluminum, manganese, and nickel including cobalt. Residual elements may be present in cast copper-base alloys. The fractured bars shall be retained for chemical verification. Both the Brinell hardness reading and Rockwell hardness reading shall be taken on the grip end of the tension test bar. At the request of the purchaser castings shall be marked with the alloy number.
SCOPE
1.1 This specification covers requirements for continuously cast rod, bar, tube, and shapes produced from copper alloys with nominal compositions as listed in Table 1.2  
1.2 Castings produced to this specification may be manufactured for and supplied from stock. In such cases the manufacturer shall maintain heat traceability to specific manufacturing date and chemical analysis.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the requirements for UNS C95300, C95400, C95410, C95500, C95800, C87500, C87800, C87850, and C89540 copper alloy permanent mold castings for general applications. UNS C95800 copper alloy used in sea water applications should be heat treated for better corrosion resistance. In general, alloys included in this specification are weldable. Mechanical properties like the tensile strength, yield strength and elongation are determined from separately cast test bar castings and should conform to the specified requirements.
SCOPE
1.1 This specification covers requirements for copper alloy2 permanent mold castings for general applications. Nominal compositions of the alloys under this specification are shown in Table 1.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the requirements for copper-based brass or bronze centrifugal castings. Mechanical properties are determined from test bar castings and should meet the requirements listed herein. Brinell hardness readings should be taken on the grip end of tension test bars. All castings should not be repaired by welding without customer approval. UNS C95520 copper alloy castings are used in the heat treated condition only.
SCOPE
1.1 This specification covers requirements for centrifugal castings of copper-base alloys having the nominal compositions shown in Table 1.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes requirements for copper alloy sand castings for valve applications. The castings shall conform to the chemical composition requirements specified. Mechanical properties shall be determined from separately cast test bars, and shall conform with the requirements. Brinell hardness readings shall be taken in the grip end of the tension test bar and shall be made in accordance with the specified requirements.
SCOPE
1.1 This specification covers requirements for copper alloy sand castings for valve applications. Nominal compositions of the alloys defined by this specification are shown in Table 1.2  
Note 1: This specification does not cover Copper Alloy UNS Nos. C83600, C92200, C96200, and C96400. These alloys are also used in valve applications. They are covered by the following specifications:
C83600: B62  
C92200: B61  
C96200: B369  
C96400: B369  
1.2 The castings produced under this specification are used in products which may be manufactured in advance and supplied for sale from stock by the manufacturer.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the requirements for copper alloys in ingot form that shall be subjected to remelting for the manufacture of castings having the Copper Alloy UNS No. designations specified and enumerated herein. Any material and manufacturing process may be used so long as the alloy is of the required composition and mechanical characteristics, and the yielded ingot is free of defects of a kind that would render it unsuitable for remelting. Materials shall hence be sampled, prepared, and tested accordingly to examine their conformance to mechanical, chemical composition, and weldability requirements.
SCOPE
1.1 This specification covers the requirements for copper alloys in ingot and other forms including granules, nuggets, pellets, or shot for remelting for the manufacturing of castings having the Copper Alloy UNS No. designation, commercial designations and nominal composition shown in Table 1 and Table 2. Product delivered in forms other than ingot shall be upon agreement between the supplier and purchaser.    
1.2 A cross reference of Copper Alloy UNS Nos. and copper alloy casting specifications is given in Table 3.    
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers requirements for copper alloy sand castings for general applications. The components part casting may be manufactured in advance and supplied from stock. The castings shall conform to the compositional requirements for named elements specified. Mechanical properties of copper alloys such as tensile strength, yield strength, and elongation shall be determined. The castings shall not be repaired, plugged, welded, or burned in.
SCOPE
1.1 This specification covers requirements for copper alloy sand castings for general applications. Nominal compositions of the alloys defined by this specification are shown in Table 1.2 This is a composite specification replacing former documents as shown in Table 1.  
Note 1: Other copper alloy castings are included in the following ASTM Specifications: B22/B22M, B61, B62, B66, B67, B148, B176, B271/B271M, B369/B369M, B427, B505/B505M, B763/B763M, B770, and B806.  
1.2 Component part castings produced to this specification may be manufactured in advance and supplied from stock. In such cases the manufacturer shall maintain a general quality certification of all castings without specific record or date of casting for a specific casting.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the establishment of requirements for lined journal bearings for use on locomotive tenders, passenger cars, and freight equipment cars. Before lining, the brass backs shall be bored and thoroughly tinned in accordance with the best standard practice. After lining, the ends of the bearings shall be made smooth by scraping, filing, or machining. The backing metal shall conform to the requirements specified for named elements for copper alloy UNS No. C94100. The lining metal shall conform to the chemical composition requirements specified for named elements. The finished bearing representing a lot for acceptance shall be broken, either longitudinally or transversely, or both, in order to ascertain the uniformity of the grain of the metal. The chemical analysis of the lining shall be made accordingly.
SCOPE
1.1 This specification covers the establishment of requirements for lined journal bearings for use on locomotive tenders, passenger cars, and freight equipment cars. The alloy specified is UNS No. C94100.2  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes requirements for bronze castings for steam locomotive wearing parts. The following Copper Alloy UNS Nos. are specified: C93200, C93400, C93600, C93700, C93800, C94300, C94400, and C94500. The product shall be manufactured by such casting methods to produce a uniform finished product. The castings shall conform to the compositional requirements for named elements specified. The castings shall not be repaired, plugged, welded, or burned-in.
SCOPE
1.1 This specification establishes requirements for bronze castings for steam locomotive wearing parts. The following Copper Alloy UNS Nos. are specified: C93200, C93400, C93600, C93700, C93800, C94300, C94400, C94500, and C95400.2
Note 1: Historically, the alloys in this specification have been used in the applications listed in the Appendix. Actual practice may vary according to locomotive type and service.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes requirements for a high-grade steam-metal or valve-bronze alloy (Copper Alloy UNS C92200) used for component castings of valves, flanges, and fittings. Tensile strength, yield strength, and elongation shall be determined from separately cast test bars and shall meet the specified requirements. Castings shall not be plugged, welded, burned-in, or impregnated.
SCOPE
1.1 This specification2 establishes requirements for a high-grade steam-metal or valve-bronze alloy (Copper Alloy UNS No. C922003) used for component castings of valves, flanges, and fittings.  
1.2 The castings covered are used in products that may be manufactured in advance and supplied from stock by the manufacturer or other dealer.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes requirements for copper-beryllium alloy sand castings for general applications and covers Copper Alloy UNS Nos. C81400, C82000, C82200, C82400, C82500, C82510, C82600, C82800, and C96700. The product shall be manufactured by casting and thermal treatment. Castings shall conform to the chemical composition requirements prescribed for copper, nickel, silicon, beryllium, cobalt, chromium, iron, zirconium, tin, and manganese. The standard temper designations include TF00 (cast, solution and precipitation heat treated) and M01 (as sand cast). Requirements for precipitation and solution heat-treatments of castings for the purpose of determining conformance to the specified mechanical properties including tensile strength, yield strength, and elongation are detailed. Special combinations of properties such as increased ductility, electrical conductivity, dimensional accuracy, and endurance life may be obtained by special precipitation heat-treatments. Tension tests shall also meet the mechanical property requirements.
SCOPE
1.1 This specification establishes requirements for sand castings produced from copper-beryllium alloys. The following alloys are covered:    
Copper Alloy
UNS No.  
Designation  
Copper  
Nickel  
Beryllium  
C81400  
70C  
99.1  
...  
0.06  
C82000  
10C  
97  
...  
0.5  
C82200  
3C, 14C  
98  
2.0  
0.5  
C82400A  
165C, 165CTA  
97.8  
...  
1.7  
C82500A  
20C, 20CTA  
97.2  
...  
2.0  
C82510  
21C  
96.6  
...  
2.0  
C82600A  
245C, 245CTA  
96.8  
...  
2.4  
C82800A  
275C, 275CTA  
96.6  
...  
2.6  
C96700  
72C  
67.2  
31.0  
1.2  
1.2 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following safety hazard caveat pertains only to the test methods described in this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory requirements prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 The mechanical properties determined from test bars for sand, permanent mold, and centrifugal castings poured in accordance with this practice represent the properties of the metal going into castings poured from the same heat. These mechanical properties may not be the same as the properties of the corresponding castings because of the solidification effects of varying size, section, and design.  
4.2 Test bars for continuous castings are taken from the castings and therefore represent the properties of the castings.
SCOPE
1.1 This practice establishes procedures for preparing test coupons and specimens (machined and unmachined) for tension tests of copper alloys for sand, permanent mold, centrifugal and continuous castings.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes requirements for gear bronze alloy castings with Copper Alloy No. C90800, C91700, C90700, C91600, and C92900. The castings may be furnished as one of three types: static chill, centrifugal chill, or sand cast. The alloys shall be subject to tensile strength, yield strength, elongation, and Brinell hardness tests. The Brinell readings shall be taken on the grip end of the tension test bar as described in the specification.
SCOPE
1.1 This specification2 establishes requirements for alloys whose copper alloy numbers and compositions are shown in Table 1. The castings may be furnished as one of three types: static chill, centrifugal chill, or sand cast.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the requirements for threadless, seamless, and deoxidized copper pipes in straight lengths, in all nominal or standard pipe sizes, for piping systems that are assembled with brazed-joint pipe fittings. The pipe shall be produced from coppers with either UNS No. C10300 or C12200. The materials for manufacture shall be cast billets, bars, or tubes of such purity and soundness as to be suitable for processing by hot extrusion or piercing, and subsequent cold working to produce a uniform wrought structure in the finished product. Products shall be produced in the H58 (drawn general purpose) temper. Products shall be sampled and prepared, then tested accordingly to examine their conformance to dimensional (outer and inner diameters, wall thickness, cross-sectional area, theoretical weight, mass, length, and roundness or squareness), mechanical (tensile strength and Rockwell hardness), and chemical composition requirements. Products shall also meet performance requirements under microscopical examination, electromagnetic (eddy-current) test, hydrostatic test, and pneumatic test.
SCOPE
1.1 This specification establishes the requirements for copper-nickel alloy castings with nominal compositions shown in Table 1.  
1.2 Castings of these alloys are used primarily for corrosion-resistance applications such as construction or pressure vessels, particularly for marine pumps, valves, and fittings.  
1.3 These alloys are considered weldable, but they may be ordered with a weld test to ensure weldability. When extensive welding is to be performed on the casting, weldability tests should be specified in the ordering information (5.2.6) to ensure proper welding characteristics.  
1.4 Units—The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, SI units are shown in brackets. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.5 The following hazard statement applies only to Section 8, Weldability Test, of this specification.This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes requirements for sand castings produced from copper-base alloys having the alloy numbers, commercial designations, and nominal compositions. The alloys the classified according to their nominal compositions: UNS No. C95200; UNS No. C95300; UNS No. C95400; UNS No. C95410; UNS No. C95500; UNS No. C95520; UNS No. C95600; UNS No. C95700; UNS No. C95800; UNS No. C95820; and UNS No. C95900. The castings shall conform to the chemical requirements specified. Mechanical properties shall be determined from separately cast test bar castings and shall meet the requirements. Brineel and Rockwell hardness readings shall be taken on the grip end of the tension test bar and shall be made in accordance with the specified requirements.
SCOPE
1.1 This specification establishes requirements for sand castings produced from copper-base alloys having the alloy numbers,2 commercial designations, and nominal compositions shown in Table 1.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the requirements for copper-alloy die castings and covers Copper Alloy UNS Nos. C85700, C85800, C86500, C87800, C99700, and C99750. The material shall conform to the chemical composition requirements prescribed for copper, tin, lead, zinc, iron, nickel, cobalt, aluminum, manganese, silicon, antimony, sulphur, and phosphorus. Unless specified, acceptance of die castings under this specification shall not depend on mechanical properties determined by tension or impact tests. Requirements for sampling for chemical analysis, dimensions, mass, internal soundness, and pressure tightness are given.
SCOPE
1.1 This specification establishes the requirements for copper-alloy die castings. The alloys specified are Copper Alloy UNS Nos. C85470, C85700, C85800, C86500, C87800, C99700, and C99750.2  
1.2 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the general requirements common to copper alloy castings of UNS Nos. C94700, C95300, C95400, C95410, C95500, C95520, and C96800. Materials shall be sampled and prepared, then tested accordingly to examine their conformance to mechanical (tensile and yield strength, hardness, and elongation), electrical (resistivity and conductivity), dimensional, chemical composition, and grain size requirements. In the event of conflict between this specification and the individual casting product specifications, the requirements of the casting specification shall take precedence.
SIGNIFICANCE AND USE
14.1 For the purpose of determining compliance with the specified limits for requirements of the properties listed in the following table, an observed value or a calculated value shall be rounded as indicated in accordance with the rounding method of Practice E29.    
Property  
Rounded Limit for Observed or
Calculated Value  
Chemical Composition
Hardness
Electrical Resistivity
Electrical Conductivity  
nearest unit in the last right-hand significance digit used in expressing the limiting value  
Tensile Strength  
nearest ksi (5 MPa)  
Yield Strength  
Elongation  
nearest 1 %  
Grain Size:  
Under 0.060 mm  
nearest multiple of 0.005 mm  
0.060 mm and over  
nearest 0.01 mm
SCOPE
1.1 This specification establishes general requirements common to ASTM copper alloy casting specifications B22/B22M, B61, B62, B66, B67, B148, B176, B271/B271M, B369, B427, B505/B505M, B584, B763/B763M, B770, and B806. These requirements apply to the casting specifications to the extent referenced therein.  
1.1.1 In the event of conflict between this specification and a casting specification, the requirements of the casting specification shall take precedence.  
1.2 The chemical composition and other requirements not included in this specification shall be prescribed in the casting product specifications.  
1.3 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 No precise quantitative relationship can be stated between the properties of the metal in various locations of the same casting or between the properties of castings and those of a test bar casting from the same metal. (See Appendix X1.)2  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the requirements for copper nickel, ferro copper, phosphor copper, and silicon copper master alloys in ingot, shot, and waffle form to be used as addition agents for cast and wrought alloys. Any material may be used which, when melted, will form an alloy of the required composition. Any manufacturing process may be used that will yield a product uniform in composition and free of defects of a nature that would render the product unsuitable for the intended application. The product in final form shall conform to the chemical composition requirements for the specified alloy. The sample for chemical analysis shall be done as specified. Composition shall be determined as the average of results from at least two replicate determinations for each element specified. For purposes of determining compliance with the specified limits for chemical composition, an observed or calculated value shall be rounded appropriately.
SIGNIFICANCE AND USE
11.1 For purposes of determining compliance with the specified limits for chemical composition an observed or calculated value shall be rounded as indicated in accordance with the Rounding method of Practice E29.    
Property  
Rounded Unit for Observed or Calculated Value  
Chemical Composition  
Nearest unit in the last right-hand significant digit
used in expressing the limiting value
SCOPE
1.1 This specification establishes the requirements for copper nickel, ferro copper, phosphor copper, and silicon copper master alloys in ingot, shot, and waffle form to be used as addition agents for cast and wrought alloys.  
1.2 Units—Values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes requirements for an alloy having a composition of copper, tin, lead, and zinc which is used for component castings of valves, flanges, and fittings. The specimen shall have the chemical composition of major elements: copper, tin, lead zinc, nickel including cobalt. It must also be comprised of the following residual elements: iron, antimony, sulfur, phosphorus, aluminum, and silicon. Mechanical properties shall be determined from separately cast test bars. Castings shall not be repaired, plugged, welded or burned-in. Valves, flanges, and fittings shall be marked accordingly in such position as not to injure the usefulness of the casting.
SCOPE
1.1 This specification2 establishes requirements for an alloy having a composition of copper, tin, lead, and zinc, used for component castings of valves, flanges, and fittings. The common trade name of this alloy is 85-5-5-5; the correct identification is Copper Alloy UNS No. C83600.3  
1.2 The castings covered are used in products that may be manufactured in advance and supplied from stock from the manufacturer or other dealer.  
1.3 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units, which are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the requirements for UNS C86300, C90500, C91100, C91300, or C93700 bronze alloy castings for turntables, movable bridges, and bridge parts. This specification also includes bronze castings made from the same copper alloys that are suitable for use in bridges and other structures for fixed and expansion bearings in which motion is slow and intermittent. Each product should be manufactured by casting to produce a uniform finished product. Castings made from the UNS C86300 copper alloy should be subjected to Brinell hardness, tension, and compression tests while those made from UNS C91100 and C91300 should be subjected to compression tests. UNS C90500 copper alloy castings should undergo tension tests. All mechanical properties like deformation limit in compression, hardness, and yield strength are determined from separately cast test bars and should conform to the specified requirements.
SCOPE
1.1 This specification establishes requirements for bronze castings for turntables, movable bridges and bridge parts, and bronze castings suitable for use in bridges and other structures for fixed and expansion bearings in which motion is slow and intermittent. The following Copper Alloys are specified: UNS No. C86300, C90500, C91100, C91300, and C93700.
Note 1: Historically, the alloys in this specification have been used in the applications listed in Appendix X1. Actual practice may vary.2  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The following safety hazard caveat pertains only to the test method(s) described in this specification:  
1.3.1 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the requirements for copper alloys in ingot form that shall be subjected to remelting for the manufacture of castings having the Copper Alloy UNS No. designations specified and enumerated herein. Any material and manufacturing process may be used so long as the alloy is of the required composition and mechanical characteristics, and the yielded ingot is free of defects of a kind that would render it unsuitable for remelting. Materials shall hence be sampled, prepared, and tested accordingly to examine their conformance to mechanical, chemical composition, and weldability requirements.
SCOPE
1.1 This specification establishes the requirements for copper alloys in ingot and other forms including granules, nuggets, pellets, or shot for remelting for the manufacturing of castings having the Copper Alloy UNS No. designation, commercial designations and nominal composition shown in Table 1 and Table 2. Product delivered in forms other than ingot shall be upon agreement between the supplier and purchaser.    
1.2 A cross reference of Copper Alloy UNS Nos. and copper alloy casting specifications is given in Table 3.    
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes requirements for continuously cast rod, bar, tube, and shapes produced from copper alloys with nominal compositions. Castings produced to this specification may be manufactured for and supplied from stock. Mechanical tests are required only when specified by the purchaser in the purchase order. Continuous castings shall not be mechanically repaired, plugged, or burned in. Weld repairs may be made at the manufacturer's discretion. For sampling purposes, a lot shall consist of castings of the same composition and same cross-sectional dimensions, produced during the continuous operation of one casting machine, and submitted for inspection at one time unless specified otherwise. The specimen shall be comprised of the following major elements: copper, tin, lead, zinc, iron, aluminum, manganese, and nickel including cobalt. Residual elements may be present in cast copper-base alloys. The fractured bars shall be retained for chemical verification. Both the Brinell hardness reading and Rockwell hardness reading shall be taken on the grip end of the tension test bar. At the request of the purchaser castings shall be marked with the alloy number.
SCOPE
1.1 This specification establishes requirements for continuously cast rod, bar, tube, and shapes produced from copper alloys with nominal compositions as listed in Table 1.2  
1.2 Castings produced to this specification may be manufactured for and supplied from stock. In such cases the manufacturer shall maintain heat traceability to specific manufacturing date and chemical analysis.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes requirements for copper alloy sand castings for valve applications. The castings shall conform to the chemical composition requirements specified. Mechanical properties shall be determined from separately cast test bars, and shall conform with the requirements. Brinell hardness readings shall be taken in the grip end of the tension test bar and shall be made in accordance with the specified requirements.
SCOPE
1.1 This specification establishes requirements for copper alloy sand castings for valve applications. Nominal compositions of the alloys defined by this specification are shown in Table 1.2  
Note 1: This specification does not cover Copper Alloy UNS Nos. C83600, C92200, C96200, and C96400. These alloys are also used in valve applications. They are covered by the following specifications:
C83600: B62  
C92200: B61  
C96200: B369  
C96400: B369  
1.2 The castings produced under this specification are used in products which may be manufactured in advance and supplied for sale from stock by the manufacturer.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers requirements for copper alloy sand castings for general applications. The components part casting may be manufactured in advance and supplied from stock. The castings shall conform to the compositional requirements for named elements specified. Mechanical properties of copper alloys such as tensile strength, yield strength, and elongation shall be determined. The castings shall not be repaired, plugged, welded, or burned in.
SCOPE
1.1 This specification covers requirements for copper alloy sand castings for general applications. Nominal compositions of the alloys defined by this specification are shown in Table 1.2 This is a composite specification replacing former documents as shown in Table 1.  
Note 1: Other copper alloy castings are included in the following ASTM Specifications: B22/B22M, B61, B62, B66, B67, B148, B176, B271/B271M, B369/B369M, B427, B505/B505M, B763/B763M, B770, and B806.  
1.2 Component part castings produced to this specification may be manufactured in advance and supplied from stock. In such cases the manufacturer shall maintain a general quality certification of all castings without specific record or date of casting for a specific casting.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the requirements for UNS C95300, C95400, C95410, C95500, C95800, C87500, C87800, C87850, and C89540 copper alloy permanent mold castings for general applications. UNS C95800 copper alloy used in sea water applications should be heat treated for better corrosion resistance. In general, alloys included in this specification are weldable. Mechanical properties like the tensile strength, yield strength and elongation are determined from separately cast test bar castings and should conform to the specified requirements.
SCOPE
1.1 This specification establishes requirements for copper alloy2 permanent mold castings for general applications. Nominal compositions of the alloys under this specification are shown in Table 1.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the requirements for copper alloys in ingot form that shall be subjected to remelting for the manufacture of castings having the Copper Alloy UNS No. designations specified and enumerated herein. Any material and manufacturing process may be used so long as the alloy is of the required composition and mechanical characteristics, and the yielded ingot is free of defects of a kind that would render it unsuitable for remelting. Materials shall hence be sampled, prepared, and tested accordingly to examine their conformance to mechanical, chemical composition, and weldability requirements.
SCOPE
1.1 This specification establishes the requirements for copper alloys in ingot and other forms including granules, nuggets, pellets, or shot for remelting for the manufacturing of castings having the Copper Alloy UNS No. designation, commercial designations and nominal composition shown in Table 1 and Table 2. Product delivered in forms other than ingot shall be upon agreement between the supplier and purchaser.    
1.2 A cross reference of Copper Alloy UNS Nos. and copper alloy casting specifications is given in Table 3.    
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the requirements for copper-based brass or bronze centrifugal castings. Mechanical properties are determined from test bar castings and should meet the requirements listed herein. Brinell hardness readings should be taken on the grip end of tension test bars. All castings should not be repaired by welding without customer approval. UNS C95520 copper alloy castings are used in the heat treated condition only.
SCOPE
1.1 This specification establishes requirements for centrifugal castings of copper-base alloys having the nominal compositions shown in Table 1.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes requirements for continuously cast rod, bar, tube, and shapes produced from copper alloys with nominal compositions. Castings produced to this specification may be manufactured for and supplied from stock. Mechanical tests are required only when specified by the purchaser in the purchase order. Continuous castings shall not be mechanically repaired, plugged, or burned in. Weld repairs may be made at the manufacturer's discretion. For sampling purposes, a lot shall consist of castings of the same composition and same cross-sectional dimensions, produced during the continuous operation of one casting machine, and submitted for inspection at one time unless specified otherwise. The specimen shall be comprised of the following major elements: copper, tin, lead, zinc, iron, aluminum, manganese, and nickel including cobalt. Residual elements may be present in cast copper-base alloys. The fractured bars shall be retained for chemical verification. Both the Brinell hardness reading and Rockwell hardness reading shall be taken on the grip end of the tension test bar. At the request of the purchaser castings shall be marked with the alloy number.
SCOPE
1.1 This specification establishes requirements for continuously cast rod, bar, tube, and shapes produced from copper alloys with nominal compositions as listed in Table 1.2 (A) Antimony 0.07, Boron 0.001.  
1.2 Castings produced to this specification may be manufactured for and supplied from stock. In such cases the manufacturer shall maintain heat traceability to specific manufacturing date and chemical analysis.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the requirements for copper-alloy die castings and covers Copper Alloy UNS Nos. C85700, C85800, C86500, C87800, C99700, and C99750. The material shall conform to the chemical composition requirements prescribed for copper, tin, lead, zinc, iron, nickel, cobalt, aluminum, manganese, silicon, antimony, sulphur, and phosphorus. Unless specified, acceptance of die castings under this specification shall not depend on mechanical properties determined by tension or impact tests. Requirements for sampling for chemical analysis, dimensions, mass, internal soundness, and pressure tightness are given.
SCOPE
1.1 This specification establishes the requirements for copper-alloy die castings. The alloys specified are Copper Alloy UNS Nos. C85470, C85700, C85800, C86500, C87800, C99700, and C99750.2  
1.2 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the general requirements common to copper alloy castings of UNS Nos. C94700, C95300, C95400, C95410, C95500, C95520, and C96800. Materials shall be sampled and prepared, then tested accordingly to examine their conformance to mechanical (tensile and yield strength, hardness, and elongation), electrical (resistivity and conductivity), dimensional, chemical composition, and grain size requirements. In the event of conflict between this specification and the individual casting product specifications, the requirements of the casting specification shall take precedence.
SIGNIFICANCE AND USE
14.1 For the purpose of determining compliance with the specified limits for requirements of the properties listed in the following table, an observed value or a calculated value shall be rounded as indicated in accordance with the rounding method of Practice E29.    
Property  
Rounded Limit for Observed or
Calculated Value  
Chemical Composition
Hardness
Electrical Resistivity
Electrical Conductivity  
nearest unit in the last right-hand significance digit used in expressing the limiting value  
Tensile Strength  
nearest ksi (5 MPa)  
Yield Strength  
Elongation  
nearest 1 %  
Grain Size:  
Under 0.060 mm  
nearest multiple of 0.005 mm  
0.060 mm and over  
nearest 0.01 mm
SCOPE
1.1 This specification establishes general requirements common to ASTM copper alloy casting specifications B22/B22M, B61, B62, B66, B67, B148, B176, B271/B271M, B369, B427, B505/B505M, B584, B763/B763M, B770, and B806. These requirements apply to the casting specifications to the extent referenced therein.  
1.1.1 In the event of conflict between this specification and a casting specification, the requirements of the casting specification shall take precedence.  
1.2 The chemical composition and other requirements not included in this specification shall be prescribed in the casting product specifications.  
1.3 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 No precise quantitative relationship can be stated between the properties of the metal in various locations of the same casting or between the properties of castings and those of a test bar casting from the same metal. (See Appendix X1.)2

ABSTRACT
This specification establishes the requirements for copper alloys in ingot form that shall be subjected to remelting for the manufacture of castings having the Copper Alloy UNS No. designations specified and enumerated herein. Any material and manufacturing process may be used so long as the alloy is of the required composition and mechanical characteristics, and the yielded ingot is free of defects of a kind that would render it unsuitable for remelting. Materials shall hence be sampled, prepared, and tested accordingly to examine their conformance to mechanical, chemical composition, and weldability requirements.
SCOPE
1.1 This specification establishes the requirements for copper alloys in ingot form for remelting for the manufacturing of castings having the Copper Alloy UNS No. designation, commercial designations and nominal composition shown in Table 1 and Table 2.  (A) Phosphorus 0.13.(B) Phosphorus 0.04.(C) Phosphorus 0.12.(D) Bismuth 5.0.(E) Selenium 0.5.(F) Selenium 0.9.(G) Selenium 0.20.(H) Selenium 0.03.(I) Phosphorus 0.1(J) Antimony 0.07, Boron 0.001.  (A) When fine grained castings are specified, 0.02–0.12 titanium is added.  
1.2 A cross reference of Copper Alloy UNS Nos. and copper alloy casting specifications is given in Table 3.    
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification establishes the requirements for threadless, seamless, and deoxidized copper pipes in straight lengths, in all nominal or standard pipe sizes, for piping systems that are assembled with brazed-joint pipe fittings. The pipe shall be produced from coppers with either UNS No. C10300 or C12200. The materials for manufacture shall be cast billets, bars, or tubes of such purity and soundness as to be suitable for processing by hot extrusion or piercing, and subsequent cold working to produce a uniform wrought structure in the finished product. Products shall be produced in the H58 (drawn general purpose) temper. Products shall be sampled and prepared, then tested accordingly to examine their conformance to dimensional (outer and inner diameters, wall thickness, cross-sectional area, theoretical weight, mass, length, and roundness or squareness), mechanical (tensile strength and Rockwell hardness), and chemical composition requirements. Products shall also meet performance requirements under microscopical examination, electromagnetic (eddy-current) test, hydrostatic test, and pneumatic test.
SCOPE
1.1 This specification establishes the requirements for copper-nickel alloy castings with nominal compositions shown in Table 1. These are as follows:2    
Copper Alloy UNS No.2  
Previous Designation  
C96200  
Alloy A  
C96400  
Alloy B  
1.2 Castings of these alloys are used primarily for corrosion-resistance applications such as in construction and for pressure vessels, particularly in marine pumps, valves, and fittings.  
1.3 These alloys are considered weldable, but they may be ordered with a weld test to ensure weldability. When extensive welding is to be performed on the casting, weldability tests should be specified in the ordering information (5.2.6) to ensure proper welding characteristics.  
1.4 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 The following hazard statement applies only to Section 8, Weldability Test, of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification establishes requirements for bronze castings for steam locomotive wearing parts. The following Copper Alloy UNS Nos. are specified: C93200, C93400, C93600, C93700, C93800, C94300, C94400, and C94500. The product shall be manufactured by such casting methods to produce a uniform finished product. The castings shall conform to the compositional requirements for named elements specified. The castings shall not be repaired, plugged, welded, or burned-in.
SCOPE
1.1 This specification establishes requirements for bronze castings for steam locomotive wearing parts. The following Copper Alloy UNS Nos. are specified: C93200, C93400, C93600, C93700, C93800, C94300, C94400, C94500, and C95400.2
Note 1: Historically, the alloys in this specification have been used in the applications listed in the Appendix. Actual practice may vary according to locomotive type and service.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification establishes the requirements for copper-based brass or bronze centrifugal castings. Mechanical properties are determined from test bar castings and should meet the requirements listed herein. Brinell hardness readings should be taken on the grip end of tension test bars. All castings should not be repaired by welding without customer approval. UNS C95520 copper alloy castings are used in the heat treated condition only.
SCOPE
1.1 This specification establishes requirements for centrifugal castings of copper-base alloys having the nominal compositions shown in Table 1. (A) Phosphorus 0.13  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification establishes requirements for copper alloy sand castings for valve applications. The castings shall conform to the chemical composition requirements specified. Mechanical properties shall be determined from separately cast test bars, and shall conform with the requirements. Brinell hardness readings shall be taken in the grip end of the tension test bar and shall be made in accordance with the specified requirements.
SCOPE
1.1 This specification establishes requirements for copper alloy sand castings for valve applications. Nominal compositions of the alloys defined by this specification are shown in Table 1.2  (A) Phosphorus 0.13(B) Phosphorus 0.1(C) Antimony 0.07, Boron 0.001.  
Note 1: This specification does not cover Copper Alloy UNS Nos. C83600, C92200, C96200, and C96400. These alloys are also used in valve applications. They are covered by the following specifications:
C83600: B62  
C92200: B61  
C96200: B369  
C96400: B369  
1.2 The castings produced under this specification are used in products which may be manufactured in advance and supplied for sale from stock by the manufacturer.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification covers the requirements for UNS C86300, C90500, C91100, C91300, or C93700 bronze alloy castings for turntables, movable bridges, and bridge parts. This specification also includes bronze castings made from the same copper alloys that are suitable for use in bridges and other structures for fixed and expansion bearings in which motion is slow and intermittent. Each product should be manufactured by casting to produce a uniform finished product. Castings made from the UNS C86300 copper alloy should be subjected to Brinell hardness, tension, and compression tests while those made from UNS C91100 and C91300 should be subjected to compression tests. UNS C90500 copper alloy castings should undergo tension tests. All mechanical properties like deformation limit in compression, hardness, and yield strength are determined from separately cast test bars and should conform to the specified requirements.
SCOPE
1.1 This specification establishes requirements for bronze castings for turntables, movable bridges and bridge parts, and bronze castings suitable for use in bridges and other structures for fixed and expansion bearings in which motion is slow and intermittent. The following Copper Alloys are specified: UNS No. C86300, C90500, C91100, C91300, and C93700.
Note 1: Historically, the alloys in this specification have been used in the applications listed in Appendix X1. Actual practice may vary.2  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The following safety hazard caveat pertains only to the test method(s) described in this specification:  
1.3.1 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification establishes requirements for a high-grade steam-metal or valve-bronze alloy (Copper Alloy UNS C92200) used for component castings of valves, flanges, and fittings. Tensile strength, yield strength, and elongation shall be determined from separately cast test bars and shall meet the specified requirements. Castings shall not be plugged, welded, burned-in, or impregnated.
SCOPE
1.1 This specification2 establishes requirements for a high-grade steam-metal or valve-bronze alloy (Copper Alloy UNS No. C922003) used for component castings of valves, flanges, and fittings.  
1.2 The castings covered are used in products that may be manufactured in advance and supplied from stock by the manufacturer or other dealer.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification establishes requirements for gear bronze alloy castings with Copper Alloy No. C90800, C91700, C90700, C91600, and C92900. The castings may be furnished as one of three types: static chill, centrifugal chill, or sand cast. The alloys shall be subject to tensile strength, yield strength, elongation, and Brinell hardness tests. The Brinell readings shall be taken on the grip end of the tension test bar as described in the specification.
SCOPE
1.1 This specification2 establishes requirements for alloys whose copper alloy numbers and nominal compositions are shown in Table 1. The castings may be furnished as one of three types: static chill, centrifugal chill, or sand cast.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification establishes requirements for copper-beryllium alloy sand castings for general applications and covers Copper Alloy UNS Nos. C81400, C82000, C82200, C82400, C82500, C82510, C82600, C82800, and C96700. The product shall be manufactured by casting and thermal treatment. Castings shall conform to the chemical composition requirements prescribed for copper, nickel, silicon, beryllium, cobalt, chromium, iron, zirconium, tin, and manganese. The standard temper designations include TF00 (cast, solution and precipitation heat treated) and M01 (as sand cast). Requirements for precipitation and solution heat-treatments of castings for the purpose of determining conformance to the specified mechanical properties including tensile strength, yield strength, and elongation are detailed. Special combinations of properties such as increased ductility, electrical conductivity, dimensional accuracy, and endurance life may be obtained by special precipitation heat-treatments. Tension tests shall also meet the mechanical property requirements.
SCOPE
1.1 This specification establishes requirements for copper-beryllium alloy sand castings for general applications and nominal compositions alloys defined by this specification are shown in Table 1.2 (A) When fine-grained castings are specified, 0.02 to 0.12 titanium is added for grain refinement, usually in the remelt ingot. See Specification B30.  
1.2 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following safety hazard caveat pertains only to the test methods described in this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory requirements prior to use.

ABSTRACT
This specification establishes requirements for an alloy having a composition of copper, tin, lead, and zinc which is used for component castings of valves, flanges, and fittings. The specimen shall have the chemical composition of major elements: copper, tin, lead zinc, nickel including cobalt. It must also be comprised of the following residual elements: iron, antimony, sulfur, phosphorus, aluminum, and silicon. Mechanical properties shall be determined from separately cast test bars. Castings shall not be repaired, plugged, welded or burned-in. Valves, flanges, and fittings shall be marked accordingly in such position as not to injure the usefulness of the casting.
SCOPE
1.1 This specification2 establishes requirements for an alloy having a composition of copper, tin, lead, and zinc, used for component castings of valves, flanges, and fittings. The common trade name of this alloy is 85-5-5-5; the correct identification is Copper Alloy UNS No. C83600.3  
1.2 The castings covered are used in products that may be manufactured in advance and supplied from stock from the manufacturer or other dealer.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification establishes the requirements for copper-based brass or bronze centrifugal castings. Mechanical properties are determined from test bar castings and should meet the requirements listed herein. Brinell hardness readings should be taken on the grip end of tension test bars. All castings should not be repaired by welding without customer approval. UNS C95520 copper alloy castings are used in the heat treated condition only.
SCOPE
1.1 This specification establishes requirements for centrifugal castings of copper-base alloys having the nominal compositions shown in Table 1. (A) Phosphorus 0.13  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification establishes the requirements for copper alloys in ingot form that shall be subjected to remelting for the manufacture of castings having the Copper Alloy UNS No. designations specified and enumerated herein. Any material and manufacturing process may be used so long as the alloy is of the required composition and mechanical characteristics, and the yielded ingot is free of defects of a kind that would render it unsuitable for remelting. Materials shall hence be sampled, prepared, and tested accordingly to examine their conformance to mechanical, chemical composition, and weldability requirements.
SCOPE
1.1 This specification establishes the requirements for copper alloys in ingot form for remelting for the manufacturing of castings having the Copper Alloy UNS No. designation, commercial designations and nominal composition shown in Table 1 and Table 2.  (A) Phosphorus 0.13.(B) Phosphorus 0.04.(C) Phosphorus 0.12.(D) Bismuth 5.0.(E) Selenium 0.5.(F) Selenium 0.9.(G) Selenium 0.20.(H) Selenium 0.03.(I) Phosphorus 0.1(J) Antimony 0.07, Boron 0.001.  (A) When fine grained castings are specified, 0.02–0.12 titanium is added.  
1.2 A cross reference of Copper Alloy UNS Nos. and copper alloy casting specifications is given in Table 3.    
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification establishes requirements for continuously cast rod, bar, tube, and shapes produced from copper alloys with nominal compositions. Castings produced to this specification may be manufactured for and supplied from stock. Mechanical tests are required only when specified by the purchaser in the purchase order. Continuous castings shall not be mechanically repaired, plugged, or burned in. Weld repairs may be made at the manufacturer's discretion. For sampling purposes, a lot shall consist of castings of the same composition and same cross-sectional dimensions, produced during the continuous operation of one casting machine, and submitted for inspection at one time unless specified otherwise. The specimen shall be comprised of the following major elements: copper, tin, lead, zinc, iron, aluminum, manganese, and nickel including cobalt. Residual elements may be present in cast copper-base alloys. The fractured bars shall be retained for chemical verification. Both the Brinell hardness reading and Rockwell hardness reading shall be taken on the grip end of the tension test bar. At the request of the purchaser castings shall be marked with the alloy number.
SCOPE
1.1 This specification establishes requirements for continuously cast rod, bar, tube, and shapes produced from copper alloys with nominal compositions as listed in Table 1.2
1.2 Castings produced to this specification may be manufactured for and supplied from stock. In such cases the manufacturer shall maintain heat traceability to specific manufacturing date and chemical analysis.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification covers requirements for copper alloy sand castings for general applications. The components part casting may be manufactured in advance and supplied from stock. The castings shall conform to the compositional requirements for named elements specified. Mechanical properties of copper alloys such as tensile strength, yield strength, and elongation shall be determined. The castings shall not be repaired, plugged, welded, or burned in.
SCOPE
1.1 This specification covers requirements for copper alloy sand castings for general applications. Nominal compositions of the alloys defined by this specification are shown in Table 1.2 This is a composite specification replacing former documents as shown in Table 1. Note 1—Other copper alloy castings are included in the following ASTM Specifications: B22/B22M, B61, B62, B66, B67, B148, B176, B271/B271M, B369, B427, B505/B505M, B763/B763M, B770, and B806.  
1.2 Component part castings produced to this specification may be manufactured in advance and supplied from stock. In such cases the manufacturer shall maintain a general quality certification of all castings without specific record or date of casting for a specific casting.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification covers the requirements for UNS C95300, C95400, C95410, C95500, C95800, C87500, C87800, C87850, and C89540 copper alloy permanent mold castings for general applications. UNS C95800 copper alloy used in sea water applications should be heat treated for better corrosion resistance. In general, alloys included in this specification are weldable. Mechanical properties like the tensile strength, yield strength and elongation are determined from separately cast test bar castings and should conform to the specified requirements.
SCOPE
1.1 This specification establishes requirements for copper alloy2 permanent mold castings for general applications. Nominal compositions of the alloys under this specification are shown in Table 1.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification covers the establishment of requirements for lined journal bearings for use on locomotive tenders, passenger cars, and freight equipment cars. Before lining, the brass backs shall be bored and thoroughly tinned in accordance with the best standard practice. After lining, the ends of the bearings shall be made smooth by scraping, filing, or machining. The backing metal shall conform to the requirements specified for named elements for copper alloy UNS No. C94100. The lining metal shall conform to the chemical composition requirements specified for named elements. The finished bearing representing a lot for acceptance shall be broken, either longitudinally or transversely, or both, in order to ascertain the uniformity of the grain of the metal. The chemical analysis of the lining shall be made accordingly.
SCOPE
1.1 This specification covers the establishment of requirements for lined journal bearings for use on locomotive tenders, passenger cars, and freight equipment cars. The alloy specified is UNS No. C94100.2  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification establishes the requirements for copper-based brass or bronze centrifugal castings. Mechanical properties are determined from test bar castings and should meet the requirements listed herein. Brinell hardness readings should be taken on the grip end of tension test bars. All castings should not be repaired by welding without customer approval. UNS C95520 copper alloy castings are used in the heat treated condition only.
SCOPE
1.1 This specification establishes requirements for centrifugal castings of copper-base alloys having the nominal compositions shown in Table 1.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification establishes requirements for sand castings produced from copper-base alloys having the alloy numbers, commercial designations, and nominal compositions. The alloys the classified according to their nominal compositions: UNS No. C95200; UNS No. C95300; UNS No. C95400; UNS No. C95410; UNS No. C95500; UNS No. C95520; UNS No. C95600; UNS No. C95700; UNS No. C95800; UNS No. C95820; and UNS No. C95900. The castings shall conform to the chemical requirements specified. Mechanical properties shall be determined from separately cast test bar castings and shall meet the requirements. Brineel and Rockwell hardness readings shall be taken on the grip end of the tension test bar and shall be made in accordance with the specified requirements.
SCOPE
1.1 This specification establishes requirements for sand castings produced from copper-base alloys having the alloy numbers,2 commercial designations, and nominal compositions shown in Table 1.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

SIGNIFICANCE AND USE
4.1 The mechanical properties determined from test bars for sand, permanent mold, and centrifugal castings poured in accordance with this practice represent the properties of the metal going into castings poured from the same heat. These mechanical properties may not be the same as the properties of the corresponding castings because of the solidification effects of varying size, section, and design.  
4.2 Test bars for continuous castings are taken from the castings and therefore represent the properties of the castings.
SCOPE
1.1 This practice establishes procedures for preparing test coupons and specimens (machined and unmachined) for tension tests of copper alloys for sand, permanent mold, centrifugal and continuous castings.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification establishes requirements for copper alloy sand castings for valve applications. The castings shall conform to the chemical composition requirements specified. Mechanical properties shall be determined from separately cast test bars, and shall conform with the requirements. Brinell hardness readings shall be taken in the grip end of the tension test bar and shall be made in accordance with the specified requirements.
SCOPE
1.1 This specification establishes requirements for copper alloy sand castings for valve applications. Nominal compositions of the alloys defined by this specification are shown in Table 1.2 Note 1—This specification does not cover Copper Alloy UNS Nos. C83600, C92200, C96200, and C96400. These alloys are also used in valve applications. They are covered by the following specifications:
C83600: B62  
C92200: B61  
C96200: B369  
C96400: B369
1.2 The castings produced under this specification are used in products which may be manufactured in advance and supplied for sale from stock by the manufacturer.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification covers the requirements for UNS C86300, C90500, C91100, C91300, or C93700 bronze alloy castings for turntables, movable bridges, and bridge parts. This specification also includes bronze castings made from the same copper alloys that are suitable for use in bridges and other structures for fixed and expansion bearings in which motion is slow and intermittent. Each product should be manufactured by casting to produce a uniform finished product. Castings made from the UNS C86300 copper alloy should be subjected to Brinell hardness, tension, and compression tests while those made from UNS C91100 and C91300 should be subjected to compression tests. UNS C90500 copper alloy castings should undergo tension tests. All mechanical properties like deformation limit in compression, hardness, and yield strength are determined from separately cast test bars and should conform to the specified requirements.
SCOPE
1.1 This specification establishes requirements for bronze castings for turntables, movable bridges and bridge parts, and bronze castings suitable for use in bridges and other structures for fixed and expansion bearings in which motion is slow and intermittent. The following Copper Alloys are specified: UNS No. C86300, C90500, C91100, C91300, and C93700.Note 1—Historically, the alloys in this specification have been used in the applications listed in Appendix X1. Actual practice may vary.2  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.