ISO 20029-2:2017
(Main)Plastics — Thermoplastic polyester/ester and polyether/ester elastomers for moulding and extrusion — Part 2: Preparation of test specimens and determination of properties
Plastics — Thermoplastic polyester/ester and polyether/ester elastomers for moulding and extrusion — Part 2: Preparation of test specimens and determination of properties
ISO 20029-2:2017 specifies the methods of preparation of test specimens and the standard test methods to be used in determining the properties of thermoplastic polyester/ester and polyether/ester elastomer moulding and extrusion materials. Requirements for handling test material and/or conditioning both the test material before moulding and the specimens before testing are given. Procedures and conditions for the preparation of test specimens in a specified state and procedures for measuring properties of the materials from which these specimens are made are given. Properties and test methods which are suitable and necessary to characterize thermoplastic polyester/ester and polyether/ester moulding and extrusion materials are listed. The properties have been selected from the general test methods in ISO 10350‑1. Other test methods in wide use for or of particular significance to these moulding and extrusion materials are also included in this document, as are the designatory properties specified in ISO 20029‑1 (hardness, melting temperature and tensile/flexural modulus). In order to obtain reproducible and comparable test results, it is intended to use the methods of preparation and conditioning, the specimen dimensions and the test procedures specified in this document. Values determined will not necessarily be identical to those obtained using specimens of different dimensions or prepared using different procedures. ISO 20029-2:2017 has been developed on the basis of ISO 10350‑1, as at the moment, no standard exists for the acquisition and presentation of comparable single-point data for thermoplastic elastomers. After publication of this document and the analogous document for polyurethanes (ISO 16365‑2), it is the intention to develop ISO 10350‑3 for the acquisition and presentation of comparable single-point data for thermoplastic elastomers, based on this document and ISO 16365‑2, as the basis for the development of thermoplastic-elastomer material standards.
Plastiques — Élastomères thermoplastiques à base de polyester/ester et polyéther/ester pour moulage et extrusion — Partie 2: Préparation des éprouvettes et détermination des propriétés
ISO 20029-2:2017 spécifie les méthodes de préparation des éprouvettes et les méthodes d'essai normalisées à utiliser pour déterminer les propriétés des élastomères thermoplastiques à base de polyester/ester et polyéther/ester pour moulage et extrusion. Les exigences relatives à la manipulation du matériau d'essai et/ou au conditionnement du matériau d'essai avant moulage et des éprouvettes avant essai sont indiquées. Les modes opératoires et les conditions nécessaires à la préparation des éprouvettes dans un état défini, ainsi que les modes opératoires de mesure des propriétés des matériaux à partir desquels les éprouvettes sont obtenues sont donnés. Les propriétés et méthodes d'essai qui sont utiles et nécessaires pour caractériser les matériaux thermoplastiques à base de polyester/ester et polyéther/ester pour moulage et extrusion sont énumérées. Les propriétés ont été sélectionnées parmi les méthodes d'essai générales de l'ISO 10350‑1. D'autres méthodes d'essai largement utilisées ou qui revêtent une importance particulière pour ces matériaux pour moulage et extrusion sont aussi incluses dans l'ISO 20029‑1 (dureté, température de fusion et module en traction/flexion). Dans le but d'obtenir des résultats d'essai reproductibles et comparables, il est prévu d'utiliser les méthodes de préparation et de conditionnement, les dimensions d'éprouvette ainsi que les modes opératoires d'essai spécifiés dans le présent document. Les valeurs déterminées ne seront pas nécessairement identiques à celles obtenues en utilisant des éprouvettes de dimensions différentes ou préparées selon des modes opératoires différents. ISO 20029-2:2017 a été élaboré sur la base de l'ISO 10350‑1 puisque, à l'heure actuelle, il n'existe aucune norme sur l'acquisition et la présentation de caractéristiques intrinsèques comparables pour les élastomères thermoplastiques. Après la publication du présent document et d'un document analogue pour les polyuréthanes (ISO 16365‑2), il est prévu d'élaborer l'ISO 10350‑3 relative à l'acquisition et la présentation de caractéristiques intrinsèques comparables pour les élastomères thermoplastiques, fondée sur le présent document et sur l'ISO 16365‑2, comme point de départ pour l'élaboration de normes couvrant les matériaux élastomères thermoplastiques.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 20029-2
First edition
2017-11
Plastics — Thermoplastic polyester/
ester and polyether/ester elastomers
for moulding and extrusion —
Part 2:
Preparation of test specimens and
determination of properties
Plastiques — Élastomères thermoplastiques à base de polyester/ester
et polyéther/ester pour moulage et extrusion —
Partie 2: Préparation des éprouvettes et détermination des propriétés
Reference number
©
ISO 2017
© ISO 2017, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2017 – All rights reserved
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 3
4 Preparation of test specimens . 3
4.1 Treatment of the material before moulding . 3
4.2 Injection moulding . 4
5 Conditioning of test specimens . 4
6 Determination of properties . 4
6.1 General . 4
6.2 Shore D hardness ≤ 25 . 6
6.2.1 Standard properties and test conditions . 6
6.2.2 Special properties and test conditions . 7
6.3 25 < Shore D hardness ≤ 65 . 8
6.3.1 Standard properties and test conditions . 8
6.3.2 Special properties and test conditions . 9
6.4 Shore D hardness > 65 .11
6.4.1 Standard properties and test conditions .11
6.4.2 Special properties and test conditions .12
Annex A (informative) Determination of tensile properties .14
Bibliography .17
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 9,
Thermoplastic materials.
This first edition of ISO 20029-2 cancels and replaces ISO 14910-2:2013, which has been technically
revised.
A list of all parts in the ISO 20029 series can be found on the ISO website.
iv © ISO 2017 – All rights reserved
Plastics
Introduction
The structure of thermoplastic elastomer material standards is based on the following considerations.
For each type of thermoplastic elastomer, reference is made to the relevant material standard.
Thermoplastic-elastomer materials are classified into three classes according to the primary
elastomeric property, hardness, as shown in Figure 1 below. This classification on the basis of hardness
reflects the special position of thermoplastic elastomers between rubber materials on the one hand
and plastics on the other.
Each class is subdivided into standard properties and special properties. The classes have many
standard properties and many special properties in common. Furthermore, a standard property in one
class can be a special property in another class and vice versa.
Special properties are those properties which are in wide use or of particular significance in the
practical characterization of a specific material.
Classi ication of TPEs
Class 1Class 2 Class 3
D ≤ 25 25 < D ≤ 65
D > 65
Standard Standard Standard
properties properties
properties
Special Special Special
properties properties properties
Figure 1 — Classification of thermoplastic elastomers on the basis of their hardness
Rubbers
INTERNATIONAL STANDARD ISO 20029-2:2017(E)
Plastics — Thermoplastic polyester/ester and polyether/
ester elastomers for moulding and extrusion —
Part 2:
Preparation of test specimens and determination of
properties
1 Scope
This document specifies the methods of preparation of test specimens and the standard test methods to
be used in determining the properties of thermoplastic polyester/ester and polyether/ester elastomer
moulding and extrusion materials. Requirements for handling test material and/or conditioning both
the test material before moulding and the specimens before testing are given.
Procedures and conditions for the preparation of test specimens in a specified state and procedures
for measuring properties of the materials from which these specimens are made are given. Properties
and test methods which are suitable and necessary to characterize thermoplastic polyester/ester and
polyether/ester moulding and extrusion materials are listed.
The properties have been selected from the general test methods in ISO 10350-1. Other test methods in
wide use for or of particular significance to these moulding and extrusion materials are also included
in this document, as are the designatory properties specified in ISO 20029-1 (hardness, melting
temperature and tensile/flexural modulus).
In order to obtain reproducible and comparable test results, it is intended to use the methods of
preparation and conditioning, the specimen dimensions and the test procedures specified in this
document. Values determined will not necessarily be identical to those obtained using specimens of
different dimensions or prepared using different procedures.
This document has been developed on the basis of ISO 10350-1, as at the moment, no standard exists for
the acquisition and presentation of comparable single-point data for thermoplastic elastomers. After
publication of this document and the analogous document for polyurethanes (ISO 16365-2), it is the
intention to develop ISO 10350-3 for the acquisition and presentation of comparable single-point data
for thermoplastic elastomers, based on this document and ISO 16365-2, as the basis for the development
of thermoplastic-elastomer material standards.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 34-1:2015, Rubber, vulcanized or thermoplastic — Determination of tear strength — Part 1: Trouser,
angle and crescent test pieces
ISO 37, Rubber, vulcanized or thermoplastic — Determination of tensile stress-strain properties
ISO 62, Plastics — Determination of water absorption
ISO 75-2, Plastics — Determination of temperature of deflection under load — Part 2: Plastics and ebonite
ISO 178, Plastics — Determination of flexural properties
ISO 179-1, Plastics — Determination of Charpy impact properties — Part 1: Non-instrumented impact test
ISO 179-2, Plastics — Determination of Charpy impact properties — Part 2: Instrumented impact test
ISO 294-1, Plastics — Injection moulding of test specimens of thermoplastic materials — Part 1: General
principles and moulding of multipurpose and bar test specimens
ISO 294-4, Plastics — Injection moulding of test specimens of thermoplastic
materials — Part 4: Determination of moulding shrinkage
ISO 306, Plastics — Thermoplastic materials — Determination of Vicat softening temperature (VST)
ISO 527-2, Plastics — Determination of tensile properties — Part 2: Test conditions for moulding and
extrusion plastics
ISO 815-1, Rubber, vulcanized or thermoplastic — Determination of compression set — Part 1: At ambient
or elevated temperatures
ISO 868, Plastics and ebonite — Determination of indentation hardness by means of a durometer (Shore
hardness)
ISO 899-1, Plastics — Determination of creep behaviour — Part 1: Tensile creep
ISO 974, Plastics — Determination of the brittleness temperature by impact
ISO 1133-2, Plastics — Determination of the melt mass-flow rate (MFR) and melt volume-flow rate (MVR)
of thermoplastics — Part 2: Method for materials sensitive to time-temperature history and/or moisture
ISO 1183-1, Plastics — Methods for determining the density of non-cellular plastics — Part 1: Immersion
method, liquid pyknometer method and titration method
ISO 1183-2, Plastics — Methods for determining the density of non-cellular plastics — Part 2: Density
gradient column method
ISO 1183-3, Plastics — Methods for determining the density of non-cellular plastics — Part 3: Gas
pyknometer method
ISO 4589-2, Plastics — Determination of burning behaviour by oxygen index — Part 2: Ambient-
temperature test
ISO 8256, Plastics — Determination of tensile-impact strength
ISO 11357-3, Plastics — Differential scanning calorimetry (DSC) — Part 3: Determination of temperature
and enthalpy of melting and crystallization
ISO 11357-4, Plastics — Differential scanning calorimetry (DSC) — Part 4: Determination of specific heat
capacity
ISO 11359-2:1999, Plastics — Thermomechanical analysis (TMA) — Part 2: Determination of coefficient of
linear thermal expansion and glass transition temperature
ISO 15512, Plastics — Determination of water content
ISO 20029-1, Plastics — Thermoplastic polyester/ester and polyether/ester elastomers for moulding and
extrusion — Part 1: Designation system and basis for specification
ISO 20753, Plastics — Test specimen
ISO 22007-2, Plastics — Determination of thermal condu
...
NORME ISO
INTERNATIONALE 20029-2
Première édition
2017-11
Plastiques — Élastomères
thermoplastiques à base de polyester/
ester et polyéther/ester pour moulage
et extrusion —
Partie 2:
Préparation des éprouvettes et
détermination des propriétés
Plastics — Thermoplastic polyester/ester and polyether/ester
elastomers for moulding and extrusion —
Part 2: Preparation of test specimens and determination of properties
Numéro de référence
©
ISO 2017
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2017, Publié en Suisse
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2017 – Tous droits réservés
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 3
4 Préparation des éprouvettes . 3
4.1 Traitement du matériau avant moulage . 3
4.2 Moulage par injection . 4
5 Conditionnement des éprouvettes . 4
6 Détermination des propriétés . 4
6.1 Généralités . 4
6.2 Dureté Shore D ≤ 25. 7
6.2.1 Propriétés normalisées et conditions d’essai . 7
6.2.2 Propriétés spéciales et conditions d’essai . 8
6.3 25 < dureté Shore D ≤ 65 .10
6.3.1 Propriétés normalisées et conditions d’essai .10
6.3.2 Propriétés spéciales et conditions d’essai .12
6.4 Dureté Shore D > 65.13
6.4.1 Propriétés normalisées et conditions d’essai .13
6.4.2 Propriétés spéciales et conditions d’essai .15
Annexe A (informative) Détermination des propriétés en traction .17
Bibliographie .20
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www.
iso.org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 61, Plastiques, sous-comité SC 9,
Matériaux thermoplastiques.
Cette première édition de l’ISO 20029-2 annule et remplace l’ISO 14910-2:2013, qui a fait l’objet d’une
révision technique.
Une liste de toutes les parties de la série ISO 20029 est disponible sur le site web de l’ISO.
iv © ISO 2017 – Tous droits réservés
Introduction
La structure des normes relatives aux matériaux élastomères thermoplastiques est fondée sur les
considérations suivantes.
Pour chaque type d’élastomère thermoplastique, il est fait référence à la norme de matériau
correspondante.
Les matériaux élastomères thermoplastiques sont divisés en trois classes en fonction de la propriété
élastomérique principale, la dureté, comme illustré à la Figure 1 ci-dessous. Cette classification sur la
base de la dureté reflète la position particulière des élastomères thermoplastiques qui se situent entre
les matériaux à base de caoutchouc et les matériaux plastiques.
Chaque classe est subdivisée en propriétés normalisées et en propriétés spéciales. Les classes possèdent
de nombreuses propriétés normalisées et de nombreuses propriétés spéciales en commun. De plus,
une propriété normalisée dans une classe peut être une propriété spéciale dans une classe voisine et
inversement.
Les propriétés spéciales sont des propriétés qui sont largement utilisées ou qui revêtent une importance
particulière dans la pratique pour la caractérisation de matériaux spécifiques.
Figure 1 — Classification des élastomères thermoplastiques sur la base de leur dureté
NORME INTERNATIONALE ISO 20029-2:2017(F)
Plastiques — Élastomères thermoplastiques à base de
polyester/ester et polyéther/ester pour moulage et
extrusion —
Partie 2:
Préparation des éprouvettes et détermination des
propriétés
1 Domaine d’application
Le présent document spécifie les méthodes de préparation des éprouvettes et les méthodes d’essai
normalisées à utiliser pour déterminer les propriétés des élastomères thermoplastiques à base de
polyester/ester et polyéther/ester pour moulage et extrusion. Les exigences relatives à la manipulation
du matériau d’essai et/ou au conditionnement du matériau d’essai avant moulage et des éprouvettes
avant essai sont indiquées.
Les modes opératoires et les conditions nécessaires à la préparation des éprouvettes dans un état
défini, ainsi que les modes opératoires de mesure des propriétés des matériaux à partir desquels les
éprouvettes sont obtenues sont donnés. Les propriétés et méthodes d’essai qui sont utiles et nécessaires
pour caractériser les matériaux thermoplastiques à base de polyester/ester et polyéther/ester pour
moulage et extrusion sont énumérées.
Les propriétés ont été sélectionnées parmi les méthodes d’essai générales de l’ISO 10350-1. D’autres
méthodes d’essai largement utilisées ou qui revêtent une importance particulière pour ces matériaux
pour moulage et extrusion sont aussi incluses dans l’ISO 20029-1 (dureté, température de fusion et
module en traction/flexion).
Dans le but d’obtenir des résultats d’essai reproductibles et comparables, il est prévu d’utiliser les
méthodes de préparation et de conditionnement, les dimensions d’éprouvette ainsi que les modes
opératoires d’essai spécifiés dans le présent document. Les valeurs déterminées ne seront pas
nécessairement identiques à celles obtenues en utilisant des éprouvettes de dimensions différentes ou
préparées selon des modes opératoires différents.
Le présent document a été élaboré sur la base de l’ISO 10350-1 puisque, à l’heure actuelle, il n’existe
aucune norme sur l’acquisition et la présentation de caractéristiques intrinsèques comparables pour les
élastomères thermoplastiques. Après la publication du présent document et d’un document analogue
pour les polyuréthanes (ISO 16365-2), il est prévu d’élaborer l’ISO 10350-3 relative à l’acquisition et
la présentation de caractéristiques intrinsèques comparables pour les élastomères thermoplastiques,
fondée sur le présent document et sur l’ISO 16365-2, comme point de départ pour l’élaboration de
normes couvrant les matériaux élastomères thermoplastiques.
2 Références normatives
Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des
exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour les
références non datées, la dernière édition du document de référence s’applique (y compris les éventuels
amendements).
ISO 34-1:2015, Caoutchouc vulcanisé ou thermoplastique — Détermination de la résistance au
déchirement — Partie 1: Éprouvettes pantalon, angulaire et croissant
ISO 37, Caoutchouc vulcanisé ou thermoplastique — Détermination des caractéristiques de contrainte-
déformation en traction
ISO 62, Plastiques — Détermination de l’absorption d’eau
ISO 75-2, Plastiques — Détermination de la température de fléchissement sous charge — Partie 2: Plastiques
et ébonite
ISO 178, Plastiques — Détermination des propriétés en flexion
ISO 179-1, Plastiques — Détermination de la résistance au choc Charpy — Partie 1: Essai de choc non
instrumenté
ISO 179-2, Plastiques — Détermination de la résistance au choc Charpy — Partie 2: Essai de choc
instrumenté
ISO 294-1, Plastiques — Moulage par injection des éprouvettes de matériaux thermoplastiques —
Partie 1: Principes généraux et moulage des éprouvettes à usages multiples et des barreaux
ISO 294-4, Plastiques — Moulage par injection des éprouvettes de matériaux thermoplastiques —
Partie 4: Détermination du retrait au moulage
ISO 306, Plastiques — Matières thermoplastiques — Détermination de la température de ramollissement
Vicat (VST)
ISO 527-2, Plastiques — Détermination des propriétés en traction — Partie 2: Conditions d’essai des
plastiques pour moulage et extrusion
ISO 815-1, Caoutchouc vulcanisé ou thermoplastique — Détermination de la déformation rémanente après
compression — Partie 1: A températures ambiantes ou élevées
ISO 868, Plastiques et ébonite — Détermination de la dureté par pénétration au moyen d’un duromètre
(dureté Shore)
ISO 899-1, Plastiques — Détermination du comportement au fluage — Partie 1: Fluage en traction
ISO 974, Plastiques — Détermination de la température de fragilité au choc
ISO 1133-2, Plastiques — Détermination de l’indice de fluidité à chaud des thermoplastiques, en masse
(MFR) et en volume (MVR) — Partie 2: Méthode pour les matériaux sensibles à l’historique temps-
température et/ou à l’humidité
ISO 1183-1, Plastiques — Méthodes de détermination de la masse volumique des plastiques non alvéolaires —
Partie 1: Méthode par immersion, méthode du pycnomètre en milieu liquide et méthode par titrage
ISO 1183-2, Plastiques — Méthodes de détermination de la masse volumique des plastiques non
alvéolaires — Partie 2: Méthode de la colonne à gradient de masse volum
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.