ISO 14171:2010
(Main)Welding consumables — Solid wire electrodes, tubular cored electrodes and electrode/flux combinations for submerged arc welding of non alloy and fine grain steels — Classification
Welding consumables — Solid wire electrodes, tubular cored electrodes and electrode/flux combinations for submerged arc welding of non alloy and fine grain steels — Classification
ISO 14171:2010 specifies requirements for the classification of electrode/flux combinations and weld metal in the as-welded condition and in the post-weld heat-treated condition for submerged arc welding of non alloy and fine grain steels with a minimum yield strength of up to 500 MPa or a minimum tensile strength of up to 570 MPa. One flux can be classified with different solid wire electrodes and tubular cored electrodes. The solid wire electrode is also classified separately based on chemical composition. ISO 14171:2010 is a combined specification providing for classification utilizing a system based upon the yield strength and the average impact energy for weld metal of 47 J, or utilizing a system based upon the tensile strength and the average impact energy for weld metal of 27 J.
Produits consommables pour le soudage — Fils-électrodes pleins, fils-électrodes fourrés et couples fils-flux pour le soudage à l'arc sous flux des aciers non alliés et à grains fins — Classification
L'ISO 14171:2010 spécifie les exigences de classification des couples fils-flux et du métal fondu hors dilution, à l'état brut de soudage et à l'état traité thermiquement après soudage, pour le soudage à l'arc sous flux des aciers non alliés et des aciers à grains fins ayant une limite d'élasticité minimale pouvant atteindre 500 Mpa ou une résistance à la traction minimale pouvant atteindre 570 MPa. Un flux peut être classifié avec des fils-électrodes pleins et des fils-électrodes fourrés différents. Le fil-électrode plein est également classifié séparément en fonction de sa composition chimique. L'ISO 14171:2010 est une spécification combinée permettant une classification utilisant un système basé sur la limite d'élasticité et l'énergie de rupture moyenne de 47 J d'un métal fondu hors dilution, ou utilisant un système basé sur la résistance à la traction et l'énergie de rupture moyenne de 27 J pour le métal fondu hors dilution.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 14171
Second edition
2010-10-01
Welding consumables — Solid wire
electrodes, tubular cored electrodes and
electrode/flux combinations for
submerged arc welding of non alloy and
fine grain steels — Classification
Produits consommables pour le soudage — Fils-électrodes pleins, fils-
électrodes fourrés et couples fils-flux pour le soudage à l'arc sous flux
des aciers non alliés et à grains fins — Classification
Reference number
©
ISO 2010
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.
© ISO 2010
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2010 – All rights reserved
Contents Page
Foreword .iv
Introduction.v
1 Scope.1
2 Normative references.1
3 Classification .2
4 Symbols and requirements .3
4.1 Symbol for the process.3
4.2 Symbol for tensile properties.3
4.2.1 Multi-run technique .3
4.2.2 Two-run technique .4
4.3 Symbol for the impact properties of all-weld metal or two-run welded joint.4
4.4 Symbol for type of welding flux .5
4.5 Symbol for the chemical composition .6
4.5.1 Solid wire electrodes.6
4.5.2 Tubular cored electrode/flux combinations.6
4.6 Symbol for hydrogen content of deposited metal .14
5 Mechanical tests.14
5.1 Multi-run technique .14
5.2 Two-run technique .16
6 Chemical analysis .16
7 Rounding procedure .17
8 Retest.17
9 Technical delivery conditions .17
10 Examples of designation .18
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 14171 was prepared by Technical Committee ISO/TC 44, Welding and allied processes, Subcommittee
SC 3, Welding consumables.
This second edition cancels and replaces the first edition (ISO 14171:2002), which has been technically
revised.
Requests for official interpretations of any aspect of this International Standard should be directed to the
Secretariat of ISO/TC 44/SC 3 via your national standards body. A complete listing of these bodies can be
found at www.iso.org.
iv © ISO 2010 – All rights reserved
Introduction
This International Standard recognizes that there are two somewhat different approaches in the global market
to classifying a given electrode/flux combination, and allows for either or both to be used, to suit a particular
market need. Application of either type of classification designation (or of both where suitable) identifies a
product as classified in accordance with this International Standard.
This International Standard provides a classification system for the designation of solid wire electrodes in
terms of their chemical composition, tubular cored electrodes in terms of the deposit composition obtained
with a particular submerged arc flux and, where required, electrode/flux combinations in terms of the yield
strength, tensile strength and elongation of the all-weld metal deposit. The ratio of yield to tensile strength of
weld metal is generally higher than that of parent material. Users should note that matching weld metal yield
strength to parent material yield strength does not necessarily ensure that the weld metal tensile strength
matches that of the parent material. Thus, where the application of the material requires matching tensile
strengths, selection of the consumable should be made by reference to column 3 of Table 1A or 1B, as
appropriate.
Although combinations of electrodes and fluxes supplied by individual companies may have the same
classification, the individual wire electrodes and fluxes from different companies are not interchangeable
unless verified in accordance with this International Standard.
The mechanical properties of all-weld metal test specimens used to classify the electrode/flux combinations
vary from those obtained in production joints because of differences in welding procedures such as electrode
size and parent material composition.
INTERNATIONAL STANDARD ISO 14171:2010(E)
Welding consumables — Solid wire electrodes, tubular cored
electrodes and electrode/flux combinations for submerged arc
welding of non alloy and fine grain steels — Classification
1 Scope
This International Standard specifies requirements for the classification of electrode/flux combinations and
weld metal in the as-welded condition and in the post-weld heat-treated condition for submerged arc welding
of non alloy and fine grain steels with a minimum yield strength of up to 500 MPa or a minimum tensile
strength of up to 570 MPa. One flux can be classified with different solid wire electrodes and tubular cored
electrodes. The solid wire electrode is also classified separately based on chemical composition.
This International Standard is a combined specification providing for classification utilizing a system based
upon the yield strength and the average impact energy for weld metal of 47 J, or utilizing a system based
upon the tensile strength and the average impact energy for weld metal of 27 J.
a) Clauses, subclauses, and tables which carry the suffix letter “A” are applicable only to electrode/flux
combinations and wire electrodes classified using the system based upon the yield strength and the
average impact energy for weld metal of 47 J, in accordance with this International Standard.
b) Clauses, subclauses, and tables which carry the suffix letter “B” are applicable only to electrode/flux
combinations and wire electrodes classified using the system based upon the tensile strength and the
average impact energy for weld metal of 27 J, in accordance with this International Standard.
c) Clauses, subclauses, and tables which do not have either the suffix letter “A” or the suffix letter “B” are
applicable to all electrode/flux combinations and wire electrodes classified in accordance with this
International Standard.
Fluxes for the single-run and two-run techniques are classified on the basis of the two-run technique.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 544, Welding consumables — Technical delivery conditions for filler materials and fluxes — Type of
product, dimensions, tolerances and markings
ISO 3690, Welding and allied processes — Determination of hydrogen content in arc weld metal
ISO 6847, Welding consumables — Deposition of a weld metal pad for chemical analysis
ISO 13916, Welding — Guidance on the measurement of preheating temperature, interpass temperature and
preheat maintenance temperature
ISO 14174, Welding consumables — Fluxes for submerged arc welding and electroslag welding —
Classification
ISO 14344, Welding consumables — Procurement of filler materials and fluxes
ISO 15792-1:2000, Welding consumables — Test methods — Part 1: Test methods for all-weld metal test
specimens in steel, nickel and nickel alloys
ISO 15792-2:2000, Welding consumables — Test methods — Part 2: Preparation of single-run and two-run
technique test specimens in steel
ISO 80000-1:2009, Quantities and units — Part 1:General
3 Classification
Classification designations are based upon two approaches to indicate the tensile properties and the impact
properties of the weld metal obtained with a given electrode/flux combination. The two designation
approaches include additional symbols for some other classification requirements, but not all, as is clear from
the following clauses. In most cases, a given commercial product can be classified in accordance with both
systems. Then either or both classification designations can be used for the product.
A solid wire electrode shall be classified in accordance with its chemical composition as given in Table 4A
or 4B.
An all-weld metal deposit from a tubular cored electrode shall be classified in accordance with the all-weld
metal composition, as given in Table 5A or 5B, obtained with a particular flux.
When the solid wire electrode or tubular cored electrode is classified in combination with a flux for submerged
arc welding, the classification shall be prefixed with a symbol in accordance with Clause 4 as appropriate.
The electrode/flux classification includes weld metal properties obtained with a manufacturer's specific
electrode/flux combination as given below. A wire electrode may be separately classified with the symbol for
its chemical composition in Table 4A or 4B.
3A Classification by yield strength and 47 J 3B Classification by tensile strength and 27 J
impact energy impact energy
The classification is divided into five mandatory The classification is divided into five mandatory
parts and an optional sixth part: parts and an optional sixth part:
1) the first part gives a symbol indicating the 1) the first part gives a symbol indicating the
process to be identified; process to be identified;
2) the second part gives a symbol indicating 2) the second part gives a symbol indicating
the strength and elongation of all-weld the strength and elongation of all-
...
NORME ISO
INTERNATIONALE 14171
Deuxième édition
2010-10-01
Produits consommables pour le
soudage — Fils-électrodes pleins, fils-
électrodes fourrés et couples fils-flux
pour le soudage à l'arc sous flux des
aciers non alliés et à grains fins —
Classification
Welding consumables — Solid wire electrodes, tubular cored electrodes
and electrode/flux combinations for submerged arc welding of non alloy
and fine grain steels — Classification
Numéro de référence
©
ISO 2010
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier
peut être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence
autorisant l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées
acceptent de fait la responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute
responsabilité en la matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info
du fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir
l'exploitation de ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation,
veuillez en informer le Secrétariat central à l'adresse donnée ci-dessous.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel.+ 41 22 749 01 11
Fax+ 41 22 749 09 47
E-mailcopyright@iso.org
Webwww.iso.org
Publié en Suisse
ii © ISO 2010 – Tous droits réservés
Sommaire Page
Avant-propos .iv
Introduction.v
1 Domaine d'application .1
2 Références normatives.1
3 Classification .2
4 Symboles et exigences.3
4.1 Symbole du procédé .3
4.2 Symbole des caractéristiques de traction .4
4.2.1 Technique multipasse.4
4.2.2 Technique à deux passes.4
4.3 Symbole de la résistance à la flexion par choc du métal fondu hors dilution ou de
l'assemblage soudé en deux passes.5
4.4 Symbole du type de flux de soudage .6
4.5 Symbole de la composition chimique .6
4.5.1 Fils-électrodes pleins.6
4.5.2 Couples fil-flux fourré .6
4.6 Symbole de la teneur en hydrogène du métal déposé .14
5 Essais mécaniques .14
5.1 Technique multipasse.14
5.2 Technique à deux passes.16
6 Analyse chimique .16
7 Procédure d'arrondi .17
8 Contre-essais.17
9 Conditions techniques de livraison.17
10 Exemples de désignation .17
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 14171 a été élaborée par le comité technique ISO/TC 44, Soudage et techniques connexes,
sous-comité SC 3, Produits consommables pour le soudage.
Cette deuxième édition annule et remplace la première édition (ISO 14171:2002), qui a fait l'objet d'une
révision technique.
Il convient d'adresser les demandes d'interprétation officielles de l'un quelconque des aspects de la présente
Norme internationale au secrétariat de l'ISO/TC 44/SC 3 via votre organisme national de normalisation. La
liste exhaustive de ces organismes peut être trouvée à l'adresse www.iso.org.
iv © ISO 2010 – Tous droits réservés
Introduction
La présente Norme internationale tient compte du fait qu'il y a deux approches quelque peu différentes pour
classifier, au niveau du marché mondial, un couple électrode-flux donné, et permet l'utilisation de l'une de ces
deux approches ou des deux à la fois, pour satisfaire à un besoin spécifique du marché. L'utilisation, pour la
classification, de l'un de ces deux types de désignation (ou des deux si applicable) permet l'identification d'un
produit classifié conformément à la présente Norme internationale.
La présente Norme internationale propose une classification afin de désigner les fils-électrodes pleins en
fonction de leur composition chimique, les fils-électrodes fourrés en fonction de la composition du dépôt
obtenue avec un flux pour soudage à l'arc et, si besoin est, les couples fils-flux en fonction de la limite
d'élasticité, de la résistance à la traction et de l'allongement du dépôt de métal fondu hors dilution. Le rapport
entre la limite d'élasticité et la résistance à la traction du métal fondu est généralement supérieur à celui du
matériau de base. Il convient que les utilisateurs notent qu'une bonne correspondance des limites d'élasticité
du métal fondu et du matériau de base ne garantira pas nécessairement que la résistance à la traction du
métal fondu correspondra à celle du matériau de base. Lorsque l'utilisation envisagée exige cette
correspondance, il convient de choisir le produit consommable par référence à la colonne 3 des Tableaux 1A
ou 1B.
Même si les couples de fils et de flux fournis par les différents fabricants peuvent avoir la même classification,
les fils et flux fournis isolément par des sociétés différentes ne sont pas interchangeables, sauf s'ils sont
vérifiés conformément à la présente Norme internationale.
Les propriétés mécaniques des éprouvettes de métal fondu hors dilution utilisées pour la classification des
couples électrodes-flux varient par rapport à celles obtenues en production du fait de différences dans le
mode opératoire de soudage, par exemple le diamètre de l'électrode et la composition chimique du matériau
de base.
NORME INTERNATIONALE ISO 14171:2010(F)
Produits consommables pour le soudage — Fils-électrodes
pleins, fils-électrodes fourrés et couples fils-flux pour le
soudage à l'arc sous flux des aciers non alliés et à grains
fins — Classification
1 Domaine d'application
La présente Norme internationale spécifie les exigences de classification des couples fils-flux et du métal
fondu hors dilution, à l'état brut de soudage et à l'état traité thermiquement après soudage, pour le soudage à
l'arc sous flux des aciers non alliés et des aciers à grains fins ayant une limite d'élasticité minimale pouvant
atteindre 500 Mpa ou une résistance à la traction minimale pouvant atteindre 570 MPa. Un flux peut être
classifié avec des fils-électrodes pleins et des fils-électrodes fourrés différents. Le fil-électrode plein est
également classifié séparément en fonction de sa composition chimique.
La présente Norme internationale est une spécification combinée permettant une classification utilisant un
système basé sur la limite d'élasticité et l'énergie de rupture moyenne de 47 J d'un métal fondu hors dilution,
ou utilisant un système basé sur la résistance à la traction et l'énergie de rupture moyenne de 27 J pour le
métal fondu hors dilution.
a) Les paragraphes et les tableaux portant le suffixe «A» sont applicables uniquement aux couples fils-flux
et aux fils-électrodes classifiés d'après le système basé sur la limite d'élasticité et l'énergie de rupture
moyenne de 47 J du métal fondu hors dilution conformément à la présente Norme internationale.
b) Les paragraphes et les tableaux portant le suffixe «B» sont applicables uniquement aux couples fils-flux
et aux fils-électrodes classifiés d'après le système basé sur la résistance à la traction et l'énergie de
rupture moyenne de 27 J du métal fondu hors dilution conformément à la présente Norme internationale.
c) Les paragraphes et les tableaux ne comportant ni le suffixe «A» ni le suffixe «B» sont applicables à tous
les couples fils-flux et tous les fils-électrodes classifiés conformément à la présente Norme internationale.
Les flux convenant pour la technique à une et deux passes sont classifiés sur la base du soudage en deux
passes.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent document. Pour les
références datées, seule l'édition citée s'applique. Pour les références non datées, la dernière édition du
document de référence s'applique (y compris les éventuels amendements).
ISO 544, Produits consommables pour le soudage — Conditions techniques de livraison des matériaux
d'apport et des flux — Type de produit, dimensions, tolérances et marquage
ISO 3690, Soudage et techniques connexes — Détermination de la teneur en hydrogène dans le soudage à
l'arc des métaux
ISO 6847, Produits consommables pour le soudage — Exécution d'un dépôt de métal fondu pour l'analyse
chimique
ISO 13916, Soudage — Lignes directrices pour le mesurage de la température de préchauffage, de la
température entre passes et de la température de maintien du préchauffage
ISO 14174, Produits consommables pour le soudage — Flux pour le soudage à l'arc sous flux et le soudage
électrique sous laitier — Classification
ISO 14344, Produits consommables pour le soudage — Approvisionnement en matériaux d'apport et flux
ISO 15792-1:2000, Produits consommables pour le soudage — Méthodes d'essai — Partie 1: Méthodes
d'essai pour les éprouvettes de métal fondu hors dilution pour le soudage de l'acier, du nickel et des alliages
de nickel
ISO 15792-2:2000, Produits consommables pour le soudage — Méthodes d'essai — Partie 2: Préparation
d'éprouvette en une ou deux passes en acier
ISO 80000-1:2009, Grandeurs et unités — Partie 1: Généralités
3 Classification
Les désignations classifiées sont basées sur deux systèmes pour indiquer les caractéristiques de traction et
de résistance à la flexion par choc du métal fondu hors dilution obtenu avec un couple fil-flux donné. Les deux
systèmes de désignation comportent des symboles supplémentaires pour certaines autres exigences relatives
à la classification, mais pas toutes, comme décrit dans les paragraphes suivants. Dans la plupart des cas, un
produit commercial donné peut être classifié dans les deux systèmes. Il est alors possible d'utiliser pour le
p
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.