ASTM D1144-99(2005)

(Practice)

Standard Practice for Determining Strength Development of Adhesive Bonds

Standard Practice for Determining Strength Development of Adhesive Bonds

SIGNIFICANCE AND USE
This practice contains suggested provisions for reporting strength values. Any ASTM test method for determining strength properties of adhesive bonds may be used. This practice is not intended to determine the pot or working life of two-component epoxy of similar type adhesives. Refer to Practice D 1338. It should be noted that there are adhesives whose testing requires special techniques and whose properties are difficult to reproduce from tester to tester. These variables should be kept in mind when analyzing the data obtained using this practice.
SCOPE
1.1 This practice covers the determination of the strength development of adhesive bonds when tested on a standard specimen under specified conditions of preparation and testing. It is applicable to adhesives in liquid or paste form that require curing at specified conditions of time and temperature or specific substrate preparation. It is intended primarily to be used with metal-to-metal adherends; however, plastics, woods, glass, or combinations of these may be substituted.
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
31-Mar-2005
ICS
83.180 - Adhesives
Technical Committee
D14 - Adhesives
Drafting Committee
D14.10 - Working Properties
Current Stage
Ref Project

Relations

Replaces
ASTM D1144-99 - Standard Practice for Determining Strength Development of Adhesive Bonds
Effective Date
01-Apr-2005
Replaced By
ASTM D1144-99(2011) - Standard Practice for Determining Strength Development of Adhesive Bonds
Effective Date
01-Apr-2011
Referred By
ASTM D4896-01(2016) - Standard Guide for Use of Adhesive-Bonded Single Lap-Joint Specimen Test Results
Effective Date
01-Apr-2005
Referred By
ASTM D6465-99(2016) - Standard Guide for Selecting Aerospace and General Purpose Adhesives and Sealants
Effective Date
01-Apr-2005

Buy Standard

ASTM D1144-99(2005) - Standard Practice for Determining Strength Development of Adhesive BondsASTM D1144-99(2005) - Standard Practice for Determining Strength Development of Adhesive Bonds
PreviousNext
Standard
ASTM D1144-99(2005) - Standard Practice for Determining Strength Development of Adhesive Bonds
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D1144–99(Reapproved2005)
Standard Practice for
Determining Strength Development of Adhesive Bonds
This standard is issued under the fixed designation D1144; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 3.2.2 fixture time (set time), n—theshortesttimerequiredby
an adhesive to develop handling strength such that test speci-
1.1 This practice covers the determination of the strength
mens can be removed from fixtures, unclamped, or handled
development of adhesive bonds when tested on a standard
without stressing the bond, thereby affecting bond strength.
specimen under specified conditions of preparation and testing.
3.2.3 handling strength, n—a low level of strength initially
It is applicable to adhesives in liquid or paste form that require
obtained by an adhesive that allows specimens to be handled,
curing at specified conditions of time and temperature or
moved, or unclamped without causing disruption of the curing
specific substrate preparation. It is intended primarily to be
process or affecting bond strength.
used with metal-to-metal adherends; however, plastics, woods,
glass, or combinations of these may be substituted.
4. Significance and Use
1.2 The values stated in SI units are to be regarded as the
4.1 This practice contains suggested provisions for report-
standard. The values given in parentheses are for information
ing strength values. Any ASTM test method for determining
only.
strength properties of adhesive bonds may be used. This
1.3 This standard does not purport to address all of the
practice is not intended to determine the pot or working life of
safety concerns, if any, associated with its use. It is the
two-component epoxy of similar type adhesives. Refer to
responsibility of the user of this standard to establish appro-
Practice D1338. It should be noted that there are adhesives
priate safety and health practices and determine the applica-
whose testing requires special techniques and whose properties
bility of regulatory limitations prior to use.
are difficult to reproduce from tester to tester. These variables
2. Referenced Documents should be kept in mind when analyzing the data obtained using
this practice.
2.1 ASTM Standards:
D907 Terminology of Adhesives
5. Test Specimens
D1002 Test Method forApparent Shear Strength of Single-
5.1 It is suggested that lap-type shear specimens in accor-
Lap-Joint Adhesively Bonded Metal Specimens by Ten-
dance with Test Method D1002, be used. Other types of test
sion Loading (Metal-to-Metal)
specimens may be used with agreement between the manufac-
D1338 Practice for Working Life of Liquid or Paste Adhe-
turer and the purchaser.
sives by Consistency and Bond Strength
6. Preparation of Test Specimens
3. Terminology
6.1 Prepare test specimens in accordance with Test Method
3.1 Definitions—Severaltermsinthispracticearedefinedin
D1002, or other applicable test method. Prepare the bonding
accordance with Terminology D907.
surface by a method mutually agreed upon between the
3.2 Definitions of Terms Specific to This Standard:
manufacturer and the purchaser. Vapor phase degreasing, grit
3.2.1 activator, or accelerator (surface), n—an adhesive
blasting,handabrasion,ortestingonoiledsurfacesaresomeof
curingagentthatisappliedtoabondingsurfaceforthepurpose
the methods that are available. If a surface activator or
of affecting or speeding, or both, the cure of an adhesive.
accelerator is used, apply it in accordance with the instructions
of the manufacturer. Use one- or two- surface activation as
agreed upon between the manufacturer and the purchaser.
This practice is under the jurisdiction of ASTM Committee D14 on Adhesives
Allow assembled specimens to cure at the temperature and
and is the direct responsibility of Subcommittee D14.10 on Working Properties.
period of time prescribed by the manufacturer to develop full
Current edition approved April 1, 2005. Published April 2005. Originally
strength.This is intended to determine if any post curing of the
approved in 1952. Last previous edition approved in 1999 as D1144 – 99. DOI:
10.1520/D1144-99R05.
adhesive occurs that would cause a strength increase and
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
decrease. Bond strength variability could be caused by em-
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
brittlement or a further hardening of the adhesive during the
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. cure cycle.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
D1144–99 (2005)
6.2 In addition, prepare a
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D4317-16(2023)(Specification)
Standard Specification for Polyvinyl Acetate-Based Emulsion Adhesives

ABSTRACT
This specification covers polyvinyl acetate or polyvinyl acetate copolymer resin emulsion adhesives suitable for use on wood, wood-based substrates, or plastic laminates. This does not cover the group of polyvinyl-based adhesives suitable for bonding flexible films. Adhesives are classified on the basis of water resistance at three performance levels, namely wet-use (Type 1), intermediate use (Type 2), and dry-use (Type 3). Adhesives shall conform to test requirements as performed under the following exposure conditions and treatments: dry shear at specified temperatures; two-cycle boil; 48-hour soak; humidity exposure; freeze-thaw stability; and storage life. Materials shall also adhere to physical properties such as density, nonvolatile matter, and pH.
SCOPE
1.1 This specification covers polyvinyl acetate or polyvinyl acetate copolymer resin emulsion adhesives suitable for use on wood, wood-based substrates, or plastic laminates. It does not cover the group of polyvinyl-based adhesives which are suitable for bonding flexible films.  
1.2 The adhesives are classified at three performance levels in accordance with water-resistance as shown in Table 1 and Table 2. See Section 5 for a description of the expected exposure conditions for each class of adhesive. See Table X1.1 for a classification of typical end products that are manufactured using adhesives at the three performance levels covered by this specification.    
1.3 The following index is provided as a guide to the test methods portion of this specification:    
Section  
Tests for Physical Properties  
9  
Viscosity  
9.1.1  
Density  
9.1.2  
Nonvolatiles  
9.1.3  
pH  
9.1.4  
Tests for Adhesive Bond  
10  
Block Shear Strength, Compression  
10.2  
Plywood Shear Tests  
10.3  
1.4 The values stated in SI units are to be regarded as the standard. The values given in parenthesis are for information purposes only.  
1.5 The following safety hazards caveat pertains only to the test method portion, Sections 9 and 10, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    6 pages
    English language
    sale 15% off
ASTM
ASTM D1582-98(2023)(Test Method)
Standard Test Method for Nonvolatile Content of Liquid Phenol, Resorcinol, and Melamine Adhesives

ABSTRACT
This test method covers the determination of nonvolatile content or total solids of liquid phenol, resorcinol, and melamine adhesives with or without hardener added and containing high-boiling and low-boiling volatile organic solvents or water, or both. The equipments to be used in the test shall include a petri dish, circulating-air oven, desiccator, and analytical balance. In determining the nonvolatile content of the liquid adhesives without hardener, the procedure shall include oven-drying, cooling in a desiccator, and weighing of adhesive and quartz sand . The percent nonvolatile content shall be calculated based on the amount remaining. On the other hand, the procedure for the liquid adhesives with hardener shall include oven-drying, cooling in a desiccator, and weighing of mixed adhesives. Also, the percent nonvolatile content shall be calculated based on the amount remaining.
SCOPE
1.1 This test method covers the determination of nonvolatile content or total solids of liquid phenol, resorcinol, and melamine adhesives with or without hardener (Note 1) added and containing high-boiling and low-boiling volatile organic solvents or water, or both.  
Note 1: Some low molecular weight materials in the adhesive may be lost if hardener is not used. When a hardener is used, it must be mixed in accordance with the manufacturer's instructions.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific precautions, see 5.2.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D4300-23(Test Method)
Standard Test Methods for Ability of Adhesive Films to Support or Resist the Growth of Fungi

SIGNIFICANCE AND USE
4.1 These test methods are designed to be used to determine the susceptibility of the adhesive film to biodegradation and whether the adhesive will carry into the bond line sufficient anti-fungal properties to prevent growth of fungi frequently present on the gluing equipment, on adherends, or in the adhesive as applied.  
4.2 Potato dextrose agar (PDA) provides a complete medium for the growth of fungi, while mineral salts agar (MSA) lacks a carbohydrate source and provides a less favorable medium. Use of PDA tests the adhesive film for its ability to resist the growth of fungi on its surface as well as its ability to repel a copious growth of fungi on the adjacent agar surface. Use of MSA tests the adhesive film primarily for its ability to resist the growth of fungi on its surface. When it is used, there is a reduced possibility that the growth from the agar will be mis-read as coming from the adhesive film, since fungal growth on the adjacent agar will be scant.
Note 2: The method given here using the MSA is based on Practice G21, adapted to be used with adhesives. Requirements for the use of the MSA are described in 10.2, and a mixed species of fungi is prescribed in 8.2 for the inoculum.  
4.3 The results obtained when using the procedures given in this method apply only to the species used for the testing. The test species listed in Section 8 are frequently used by laboratories to test for antifungal properties, but they are not the only ones which could be used. Selection of the fungal species to test against requires informed judgment by the testing laboratory or by the party requesting the tests. These methods are especially useful when species that have been isolated from contaminated adhesives are used as the test species (see Section 8) to aid in the selection of more effective fungicides.  
4.4 The efficacy of some biocides may change in storage due to the chemical and thermal environment to which they are subjected as components of certain adhesi...
SCOPE
1.1 These test methods test the ability of adhesive films to inhibit or support the growth of selected fungal species growing on agar plates by providing means of testing the films on two agar substrates, one which promotes microbial growth, and one which does not.  
1.2 These test methods are not appropriate for all adhesives. The activity of certain biocides may not be demonstrated by these test methods as a result of irreversible reaction with some of the medium constituents.  
Note 1: As an example, quaternary ammonium compounds are inactivated by agar.  
1.3 A test method is included for use with low-viscosity adhesives along with an alternative method for use with mastic-type adhesives.  
1.4 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. These test methods are designed to be used by persons trained in correct microbiological techniques. Specific precautionary statements are given in Section 7 and in 14.3.2.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM D3929-03(2023)(Test Method)
Standard Test Method for Evaluating Stress Cracking of Plastics by Adhesives Using the Bent-Beam Method

SIGNIFICANCE AND USE
5.1 This test method is designed for obtaining a qualitative estimate of the compatibility of plastics and adhesives. Due to the many process variables associated with the fabrication of plastic parts, it is not possible to use this test as a substitute for compatibility tests on actual parts.  
5.2 The detection of cracks or crazes may be determined with or without optical aid. Make comparisons only among tests employing crack detection methods of equivalent sensitivity.
SCOPE
1.1 This test method describes a procedure for determining the compatibility of adhesives with plastics based on whether the adhesive causes cracking of stressed samples.  
1.2 Specimen configurations and test fixture designs are given.  
1.3 This test method is suitable for products in the form of sheet or strip. It can also be used on injection molded tensile specimens or flexural bars.  
1.4 The values stated in SI units are to be regarded as the standard. The inch-pound units given in parentheses are for information only.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D4680-98(2023)(Test Method)
Standard Test Method for Creep and Time to Failure of Adhesives in Static Shear by Compression Loading (Wood-to-Wood)

SIGNIFICANCE AND USE
4.1 Creep data that are obtained over a relatively short period of time in this test method can provide a measure of an adhesive bond's ability to withstand static loading in shear over a relatively long period of time. Creep measurements are made over a range of expected service conditions, including level of stress, temperature, relative humidity, and duration of load. Creep rate, creep strain, and creep modulus are calculated at the various service conditions.  
4.2 Creep data can be used to (1) predict performance of an adhesive under long-term loading, (2) characterize an adhesive, (3) compare adhesives with each other and against specifications, and (4) design structural members fabricated with an adhesive.  
4.3 Time-to-failure data provide a measure of the ultimate load-carrying ability of an adhesive bond as a function of time at various levels of stress, temperature, and relative humidity.  
4.4 With proper caution, time-to-failure data derived from relatively short loading periods can be extrapolated to estimate the useful service life of an adhesive at working levels of static stress. This property may also be used with creep data to accomplish purposes listed in 4.2.  
4.5 This test method is a research tool intended for development or evaluation of new adhesives and new product designs. The researcher may select from suggested tests those that are appropriate. However, creep and time-to-failure tests are nonroutine and can be time-consuming and expensive, so tests must be selected with care.  
4.6 The apparatus and procedures may be suitable for measuring creep properties of adhesives on substrates other than wood, such as metal, plastic, and glass, but such considerations are not within the scope of this test method.
SCOPE
1.1 This test method covers the determination of time-dependent properties of structural adhesives in wood-to-wood bonds when specimens are subjected to shearing stresses at various levels of static load, constant temperature, and relative humidity. Apparatus and procedures are provided for direct measurement of time-dependent shear deformation (creep) and time to failure of adhesive bonds under static load. Guidelines for selecting test conditions, methods for calculating creep rate, creep strain, creep modulus, and extrapolation of time to failure, are given along with methods of presenting these data.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    10 pages
    English language
    sale 15% off
ASTM
ASTM D2095-96(2023)(Test Method)
Standard Test Method for Tensile Strength of Adhesives by Means of Bar and Rod Specimens

SIGNIFICANCE AND USE
4.1 Tension tests provide reasonably accurate information with regard to the tensile strength of adhesives. Tensile strength data may be suitable for specification acceptance, service evaluation, manufacturing control, research, and development. Tension tests are not considered significant for applications differing from the test in rate, direction, and type of loading.
SCOPE
1.1 This test method covers the determination of the relative tensile strength of adhesives by the use of bar- and rod-shaped butt-joined specimens under defined conditions of preparation, conditioning, and testing. This test method is applicable to the testing of adhesives with various adherend materials in either similar or dissimilar combinations.  
Note 1: An alternative test method for determining the tensile strength of adhesives is Test Method D897.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D3930-08(2023)(Specification)
Standard Specification for Adhesives for Wood-Based Materials for Construction of Manufactured Homes

ABSTRACT
This specification provides the means to measure and evaluate the performance of adhesives for structural or semistructural bonding of wood-to-wood in manufactured homes. Wood as used in this specification includes lumber, plywood, particleboard, gypsum board, and all materials having woodbased surfaces at the bondline. The adhesives can be classified according to resistance to deformation: Group A or structural, and Group B or semistructural. Also, the adhesives may be designated into three types, according to their recommended use based on their resistance to water and water vapor: Type 1 for interior and exterior use, Type 2 for weather-protected interior use, and Type 3 for interior use only. Different tests shall be performed in order to determine the following properties of adhesives: shear strength, gap-filling ability, total deformation resistance, moisture and temperature limitation during fabrication, high-temperature resistance, low-temperature resistance, moisture resistance, aging, oxidation resistance, and mold resistance.
SCOPE
1.1 This specification provides the means to measure and evaluate the performance of adhesives for structural or semi-structural bonding of wood-to-wood in manufactured homes. Wood as used in this specification includes lumber, plywood, particleboard, gypsum board, and all materials having wood-based surfaces at the bondline. This specification does not cover other adhesives used in manufactured homes such as adhesives for carpet, floor tile, ceramic fixtures, plastic laminates, trim and millwork, and similar nonstructural applications.  
1.1.1 The performance of the adhesives is measured in the following tests:    
Number  
Test  
Section  
1  
Low Temperature  
16  
2  
Dry Lumber  
17  
3  
Gap-Filling  
18  
4  
High Temperature  
19  
5  
Type 3 Qualification  
20  
6  
Type 2 Qualification  
21  
7  
Aging, Film Oxidation  
22  
8  
Aging, Bond Oxidation  
23  
9  
Resistance to Deformation, Creep  
24  
10  
Mold  
25  
11  
Type 1 Qualification  
26  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    19 pages
    English language
    sale 15% off
ASTM
ASTM D907-15(2023)(Terminology)
Standard Terminology of Adhesives

SCOPE
1.1 This terminology standard is a compilation of definitions used in the science and technology of the adhesives industry. Terms that are generally understood or adequately defined in other readily available sources are not included.  
1.2 Any changes in this standard since 1988 are documented as follows:  
1.2.1 Appendix X1 gives a history of revisions made since 1988. Table X1.1 lists the terms that are affected as: (1) Terms Added, (2) Terms Revised, and (3) Terms Deleted.
1.2.1.1 In Table X1.1, the year of publication in Volume 15.06 is shown in parentheses following the term.  
1.2.2 In the text of the standard, the year of publication is shown following each definition. Also, the following codes are included after the year of publication to describe the type change that was made: (A) Addition, (R) Revision, or (E) Edited.  
1.2.3 Deletions are shown in Appendix X1, suitably footnoted. The deleted terms do not appear in the text of the standard.  
1.2.4 Any special circumstances not covered by 1.2.2 and 1.2.3 are documented in Table X1.1, suitably footnoted.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    13 pages
    English language
    sale 15% off
ASTM
ASTM D7966/D7966M-16(2023)(Test Method)
Standard Test Method for Resistance to Creep of Adhesives in Static Shear by Compression Loading (Wood-to-Wood)

SIGNIFICANCE AND USE
5.1 This test method evaluates the performance of the adhesive in laminated wood as measured by resistance to creep under static load.  
5.2 Test results from the evaluation of adhesive creep resistance, under designated environmental conditions of the test, provide a measure of the adhesive’s ability to withstand constant loading over a relatively long period of time.  
5.3 Creep measured with this test method is normally used in conjunction with specifications such as, but not limited to Specification D2559 and CSA O112.9 to confirm suitability of an adhesive to resist creep under designed loads when subjected to specific levels of stress, load duration and environmental conditions.
SCOPE
1.1 This test method covers the determination of creep properties of structural adhesives in wood-to-wood bonds when a standardized specimen is subjected to shearing stresses at various levels of static load, constant temperature, and relative humidity. Apparatus and procedures are provided for shear deformation (creep) of adhesive bonds under static load. This test method is used under the indicated conditions to evaluate resistance to creep properties of a structural wood adhesive.  
1.2 The test method is used to evaluate creep performance of adhesives suitable for the bonding of wood, including treated wood, into structural wood products for general construction, marine use, or for other uses where a high-strength general construction, creep-resistant, durable adhesive bond is required. Individual block shear specimens are prepared from adhesively bonded laminations, subjected to a constant load under various combinations of temperature and relative humidity, and the amount of creep measured.  
1.3 Creep of structural wood adhesives as measured by this test method may not be comparative to other ASTM methods and is limited to the conditions of the test and procedures contained herein.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D4800-94(2023)(Guide)
Standard Guide for Classifying and Specifying Adhesives

SIGNIFICANCE AND USE
4.1 The purpose of this classification system is to provide a method of identifying adhesives in order to give industry a system that can be used universally for materials. It further provides a means for specifying these materials by the use of the standards that are developed using this guide.  
4.2 This classification system was developed to permit the addition of future adhesives.
SCOPE
1.1 This guide provides a classification system for tabulating the properties of adhesives suitable for holding parts or assemblies together. The use of this guide also provides information necessary for the development of standard specifications for adhesives.  
Note 1: This classification system may serve many of the needs of industries using adhesives. This guide is subject to revision as the need requires; therefore, the latest revision should always be used.  
1.2 Limitations—This classification system is intended to be a means of identifying adhesives. It is not intended for the selection of materials. Material selection should be made by those having expertise in the adhesives field after careful consideration of the design and the performance required of the part, the environment to which it will be exposed, the attachment process to be employed, the inherent properties of the material not covered in this document, and the economic factors.  
1.3 This classification system is based on the premise that adhesives can be arranged into broad generic families using basic properties to arrange the materials into groups, classes, and grades.  
1.4 In all cases where the provisions of this classification system would conflict with the referenced ASTM specification for a particular material, the latter shall take precedence.  
1.5 The values stated in SI units, as detailed in IEEE/ASTM SI 10, are to be regarded as the standard.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.