ISO 3785:2023
(Main)Metallic materials — Designation of test specimen axes in relation to product texture
Metallic materials — Designation of test specimen axes in relation to product texture
This document specifies a method for designating test specimen axes in relation to product texture by means of an X-Y-Z orthogonal coordinate system. This document applies equally to unnotched and notched (or precracked) test specimens. This document is intended only for metallic materials with uniform texture that can be unambiguously determined. Test specimen orientation is decided before specimen machining, identified in accordance with the designation system specified in this document, and recorded.
Matériaux métalliques — Désignation des axes des éprouvettes en relation avec la texture du produit
Le présent document spécifie une méthode pour désigner les axes des éprouvettes en relation avec la texture du produit, au moyen d'un système orthogonal de coordonnées X-Y-Z. Le présent document s'applique aussi bien aux éprouvettes sans entaille qu'aux éprouvettes entaillées (ou préfissurées). Le présent document est destiné seulement aux matériaux métalliques de texture uniforme qui peut être déterminée sans ambiguïté. L'orientation de l'éprouvette est décidée avant usinage de l'éprouvette, identifiée conformément au système de désignation spécifié dans le présent document, et enregistrée.
General Information
Relations
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 3785
Third edition
2023-05
Metallic materials — Designation
of test specimen axes in relation to
product texture
Matériaux métalliques — Désignation des axes des éprouvettes en
relation avec la texture du produit
Reference number
© ISO 2023
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Designation system . 1
4.1 General . 1
4.2 Exception — not aligned . 1
4.3 Exception — no grain flow . 2
5 Designation of unnotched specimens . 2
5.1 General . 2
5.2 Sheet, plate, bar (flat rolled products). 2
5.2.1 Aligned, grain flow different in all three orthogonal directions . 2
5.2.2 Not aligned, grain flow different in all three orthogonal directions . 2
5.2.3 Aligned, equal cross-sectional grain flow . 2
5.2.4 Not aligned, equal cross-sectional grain flow . 2
5.3 Cylinders and thick-walled tubes. 3
5.4 Thin-walled tubes, helical grain flow . 3
5.5 Castings . 3
6 Designation of notched (or precracked) specimens . 3
6.1 General . 3
6.2 Aligned . 3
6.3 Not aligned . 3
6.4 No grain flow . 3
6.5 Welds . 3
6.6 Additive manufacturing . 4
7 Application of designation system in material specification . 4
7.1 General . 4
7.2 Non-uniform grain flow. 4
7.3 Specifications . 4
7.4 Comparisons . 4
Annex A (informative) Influence of mechanical working on material structure and
properties . 8
Bibliography . 9
iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to
the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 164, Mechanical testing of metals,
Subcommittee SC 4, Fatigue, fracture and toughness testing, in collaboration with the European
Committee for Standardization (CEN) Technical Committee CEN/TC 459/SC 1, Test methods for steel
(other than chemical analysis), in accordance with the Agreement on technical cooperation between ISO
and CEN (Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 3785:2006), which has been technically
revised.
The main changes are as follows:
— a reference to Annex A was added in the Introduction;
— in 6.5 a reference to ISO 15653 was added;
— a new Subclause 6.6 (Additive manufacturing) was added.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
Introduction
The measured mechanical properties of a metallic product, especially those characterizing ductility
and toughness, such as elongation, reduction of area, fracture toughness and impact resistance, are
dependent on the test specimen location within the product and orientation with respect to the
product's principal directions of metal working, grain flow or otherwise-produced texture. This
document specifies a method for designating specimen orientation in relation to product texture.
Additional information on the influence of mechanical working on material structure and properties is
provided in Annex A.
v
INTERNATIONAL STANDARD ISO 3785:2023(E)
Metallic materials — Designation of test specimen axes in
relation to product texture
1 Scope
This document specifies a method for designating test specimen axes in relation to product texture by
means of an X-Y-Z orthogonal coordinate system.
This document applies equally to unnotched and notched (or precracked) test specimens.
This document is intended only for metallic materials with uniform texture that can be unambiguously
determined.
Test specimen orientation is decided before specimen machining, identified in accordance with the
designation system specified in this document, and recorded.
2 Normative references
There are no normative references in this document.
3 Terms and definitions
No terms and definitions are listed in this document.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
4 Designation system
4.1 General
The method for relating specimen axes to the characteristic directions of the product makes use of an
X-Y-Z orthogonal coordinate system for wrought metals:
— the letter X always denotes the direction of principal deformation (maximum grain flow in the
product);
— the letter Y denotes the direction of least deformation;
— the letter Z denotes the direction normal to the X-Y plane.
4.2 Exception — not aligned
When the specimen direction does not coincide with the product's characteristic grain-flow directions,
two letters are used as described for unnotched specimens in 5.2.2 and 5.2.4, and for notched specimens
in 6.3.
4.3 Exception — no grain flow
When there is no grain-flow direction as in a casting, specimen location and orientation shall be
specified on a part drawing and the test result shall carry no orientation designation.
5 Designation of unnotched specimens
5.1 General
The designations of unnotched specimens variously aligned with respect to the product's characteristic
grain-flow directions are depicted in Figure 1. Only specimens fully aligned with, or lying midway
between, the product's characteristic grain-flow directions are shown.
5.2 Sheet, plate, bar (flat rolled products)
5.2.1 Aligned, grain flow different in all three orthogonal directions
For products of non-circular cross-section and grain flow differing in the three orthogonal directions,
specimens aligned with the product's characteristic grain-flow directions are designated as either X-,
Y- or Z-direction specimens as depicted in Figure 1 a).
5.2.2 Not aligned, grain flow different in all three orthogonal directions
For products of non-circular cross-section and grain flow differing in the three orthogonal directions,
specimens lying midway between the product's characteristic grain-flow directions are designated
as XY-, XZ- or YZ-direction specimens as depicted in Figure 1 f). When the specimen lies neither in
alignment with the product's characteristic grain-flow directions nor midway between them, but rather
at some other angle to them, then that angle shall be stated between the two designation letters, the
first letter denoting the direction toward which the specimen axis is inclined, and the second letter the
direction from which the specimen axis is inclined. This designation scheme is restricted to direction
vectors that lie within any of the three planes de
...
NORME ISO
INTERNATIONALE 3785
Troisième édition
2023-05
Matériaux métalliques — Désignation
des axes des éprouvettes en relation
avec la texture du produit
Metallic materials — Designation of test specimen axes in relation to
product texture
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2023
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application .1
2 Références normatives .1
3 Termes et définitions . 1
4 Système de désignation . 1
4.1 Généralités . 1
4.2 Exception — Désaxé . 1
4.3 Exception — Absence de fibrage . 2
5 Désignation des éprouvettes sans entaille . 2
5.1 Généralités . 2
5.2 Tôle, plaque, barre (produits plats laminés) . 2
5.2.1 Axé, fibrage différent dans les trois directions orthogonales . 2
5.2.2 Désaxé, fibrage différent dans les trois directions orthogonales . 2
5.2.3 Axé, fibrage équiaxe . 2
5.2.4 Désaxé, fibrage équiaxe . 2
5.3 Cylindres et tubes épais . 3
5.4 Tubes à paroi mince, fibrage hélicoïdal. 3
5.5 Pièces moulées . . 3
6 Désignation des éprouvettes entaillées (ou préfissurées) . 3
6.1 Généralités . 3
6.2 Axé . 3
6.3 Désaxé . 3
6.4 Absence de fibrage . 4
6.5 Soudures . . 4
6.6 Fabrication additive . 4
7 Application du système de désignation dans les spécifications de matériaux .4
7.1 Généralités . 4
7.2 Fibrage non uniforme . 4
7.3 Spécifications . 4
7.4 Comparaisons . 4
Annexe A (informative) Influence d'une mise en forme mécanique sur la structure et les
caractéristiques des matériaux .8
Bibliographie . 9
iii
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document
a été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir: www.iso.org/iso/fr/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 164, Essais mécaniques des métaux,
sous-comité SC 4, Essais de fatigue, de fracture et de ténacité, en collaboration avec le Comité européen
de normalisation (CEN) comité technique CEN/TC 459/SC 1, Méthodes d'essai des aciers (autres que
l'analyse chimique), conformément à l'accord de coopération technique entre l'ISO et le CEN (Accord de
Vienne).
Cette troisième édition annule et remplace la deuxième édition (ISO 3785:2006), qui a fait l'objet d'une
révision technique.
Les principaux changements sont les suivants:
— une référence à l'Annexe A a été ajoutée dans l'introduction;
— en 6.5, une référence à l'ISO 15653 a été ajoutée;
— un nouveau paragraphe 6.6 (Fabrication additive) a été ajouté.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www.iso.org/fr/members.html.
iv
Introduction
Les caractéristiques mécaniques mesurées d'un produit métallique, particulièrement celles
caractérisant la ductilité et la ténacité, telles que l'allongement, la striction, la ténacité à la rupture
et la résistance au choc, dépendent de la position des éprouvettes dans le produit et de l'orientation
des éprouvettes par rapport aux directions principales de mise en forme du métal, du fibrage ou
d'autres textures formées au sein du produit. Le présent document spécifie une méthode pour désigner
l'orientation des éprouvettes en relation avec la texture du produit.
Des informations supplémentaires sur l'influence du travail mécanique sur la structure et les propriétés
des matériaux sont fournies à l'Annexe A.
v
NORME INTERNATIONALE ISO 3785:2023(F)
Matériaux métalliques — Désignation des axes des
éprouvettes en relation avec la texture du produit
1 Domaine d'application
Le présent document spécifie une méthode pour désigner les axes des éprouvettes en relation avec la
texture du produit, au moyen d'un système orthogonal de coordonnées X-Y-Z.
Le présent document s'applique aussi bien aux éprouvettes sans entaille qu'aux éprouvettes entaillées
(ou préfissurées).
Le présent document est destiné seulement aux matériaux métalliques de texture uniforme qui peut
être déterminée sans ambiguïté.
L'orientation de l'éprouvette est décidée avant usinage de l'éprouvette, identifiée conformément au
système de désignation spécifié dans le présent document, et enregistrée.
2 Références normatives
Le présent document ne contient aucune référence normative.
3 Termes et définitions
Aucun terme n’est défini dans le présent document.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse https:// www .electropedia .org/
4 Système de désignation
4.1 Généralités
La méthode pour relier les axes des éprouvettes aux directions caractéristiques du produit utilise un
système orthogonal de coordonnées X-Y-Z pour les métaux mis en forme, pour lequel:
— la lettre X dénote toujours la direction de déformation principale (fibrage maximal dans le produit);
— la lettre Y dénote la direction de moindre déformation;
— la lettre Z dénote la direction perpendiculaire au plan X-Y.
4.2 Exception — Désaxé
Lorsque la direction de l'éprouvette ne coïncide pas avec les directions de fibrage caractéristiques du
produit, deux lettres sont utilisées, comme décrit pour les éprouvettes sans entaille en 5.2.2 et en 5.2.4
et pour les éprouvettes entaillées en 6.3.
4.3 Exception — Absence de fibrage
Lorsqu'il n'y a aucune direction de fibrage, comme dans une pièce moulée, la position et l'orientation de
l'éprouvette doivent être définies sur un dessin de la pièce et aucune désignation d'orientation ne doit
être attribuée au résultat d'essai.
5 Désignation des éprouvettes sans entaille
5.1 Généralités
Les désignations des éprouvettes sans entaille, orientées différemment par rapport aux directions de
fibrage caractéristiques du produit, sont décrites à la Figure 1. Seules les éprouvettes totalement dans
l'axe des directions de fibrage caractéristiques du produit ou orientées selon les bissectrices des angles
formés par ces directions sont représentées.
5.2 Tôle, plaque, barre (produits plats laminés)
5.2.1 Axé, fibrage différent dans les trois directions orthogonales
Pour les produits de section non circulaire et de fibrage différent dans les trois directions
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.