(Main)Rubber, vulcanized or thermoplastic — Determination of hardness — Part 2: Hardness between 10 IRHD and 100 IRHD
Rubber, vulcanized or thermoplastic — Determination of hardness — Part 2: Hardness between 10 IRHD and 100 IRHD
This document specifies four methods for the determination of the hardness of vulcanized or thermoplastic rubbers on flat surfaces (standard-hardness methods) and four methods for the determination of the apparent hardness of curved surfaces (apparent-hardness methods). The hardness is expressed in international rubber hardness degrees (IRHD). The methods cover the hardness range from 10 IRHD to 100 IRHD. These methods differ primarily in the diameter of the indenting ball and the magnitude of the indenting force, these being chosen to suit the particular application. The range of applicability of each method is indicated in Figure 1. This document does not specify a method for the determination of hardness by a pocket hardness meter, which is described in ISO 48-5. This document specifies the following four methods for the determination of standard hardness. — Method N (normal test) is appropriate for rubbers with a hardness in the range 35 IRHD to 85 IRHD, but can also be used for hardnesses in the range 30 IRHD to 95 IRHD. — Method H (high-hardness test) is appropriate for rubbers with a hardness in the range 85 IRHD to 100 IRHD. — Method L (low-hardness test) is appropriate for rubbers with a hardness in the range 10 IRHD to 35 IRHD. — Method M (microtest) is essentially a scaled-down version of the normal test method N, permitting the testing of thinner and smaller test pieces. It is appropriate for rubbers with a hardness in the range 35 IRHD to 85 IRHD, but can also be used for hardnesses in the range 30 IRHD to 95 IRHD. NOTE 1 The value of the hardness obtained by method N within the ranges 85 IRHD to 95 IRHD and 30 IRHD to 35 IRHD might not agree precisely with that obtained using method H or method L, respectively. The difference is not normally significant for technical purposes. NOTE 2 Because of various surface effects in the rubber and the possibility of slight surface roughness (produced, for example, by buffing), the microtest might not always give results agreeing with those obtained by the normal test. This document also specifies four methods, CN, CH, CL and CM, for the determination of the apparent hardness of curved surfaces. These methods are modifications of methods N, H, L and M, respectively, and are used when the rubber surface tested is curved, in which case there are two possibilities: a) the test piece or product tested is large enough for the hardness instrument to rest upon it; b) the test piece or product tested is small enough for both the test piece and the instrument to rest upon a common support. A variant of b) would be where the test piece rests upon the support surface of the instrument. Apparent hardness can also be measured on non-standard flat test pieces using methods N, H, L and M. The procedures described cannot provide for all possible shapes and dimensions of test piece, but cover some of the commonest types, such as O-rings.
Caoutchouc vulcanisé ou thermoplastique — Détermination de la dureté — Partie 2: Dureté comprise entre 10 DIDC et 100 DIDC
Le présent document spécifie quatre méthodes de détermination de la dureté des caoutchoucs vulcanisés ou thermoplastiques sur des surfaces planes (méthodes de détermination de la dureté normale) et quatre méthodes de détermination de la dureté apparente sur des surfaces courbes (méthodes de détermination de la dureté apparente). La dureté est exprimée en degrés internationaux de dureté du caoutchouc (DIDC). Les méthodes couvrent les duretés comprises entre 10 DIDC et 100 DIDC. Les méthodes diffèrent principalement par le diamètre de la bille du pénétrateur et par la valeur de la force de pénétration, celles-ci étant choisies en fonction de l'application considérée. La plage d'applicabilité de chaque méthode est indiquée à la Figure 1. Le présent document ne spécifie pas de méthode de détermination de la dureté à l'aide d'un duromètre de poche, qui est décrite dans l'ISO 48-5. Le présent document spécifie les quatre méthodes suivantes pour la détermination de la dureté normale. — La méthode N (essai normal) est appropriée pour les caoutchoucs dont la dureté est comprise entre 35 DIDC et 85 DIDC, mais elle peut également être utilisée pour ceux dont la dureté est comprise entre 30 DIDC et 95 DIDC. — La méthode H (essai pour dureté élevée) est appropriée pour les caoutchoucs dont la dureté est comprise entre 85 DIDC et 100 DIDC. — La méthode L (essai pour faible dureté) est appropriée pour les caoutchoucs dont la dureté est comprise entre 10 DIDC et 35 DIDC. — La méthode M (micro-essai) est essentiellement une variante à échelle réduite de l'essai de dureté normale, méthode N, permettant des essais sur des éprouvettes de plus petites dimensions et d'épaisseur plus faible. Elle est appropriée pour les caoutchoucs dont la dureté est comprise entre 35 DIDC et 85 DIDC, mais peut également être utilisée pour ceux dont la dureté est comprise entre 30 DIDC et 95 DIDC. NOTE 1 Les valeurs de dureté obtenues avec la méthode N de 85 DIDC à 95 DIDC et de 30 DIDC à 35 DIDC peuvent ne pas exactement concorder avec celles obtenues respectivement avec la méthode H ou la méthode L. La différence est normalement négligeable pour des applications techniques. NOTE 2 En raison de l'influence de l'état de surface du caoutchouc et d'une possible légère rugosité (due, par exemple, au meulage), le micro-essai ne donne pas toujours des résultats en accord avec ceux de l'essai normal. Le présent document spécifie également quatre méthodes, CN, CH, CL et CM, de détermination de la dureté apparente sur surfaces courbes. Ces méthodes sont des variantes des méthodes N, H, L et M, respectivement, et sont utilisées lorsque la surface du caoutchouc soumis à essai est courbe, auquel cas il existe deux possibilités: a) l'éprouvette ou le produit soumis à essai est suffisamment grand(e) pour que le duromètre puisse être posé dessus; ou b) l'éprouvette ou le produit soumis à essai est suffisamment petit(e) pour que l'éprouvette et l'instrument puissent être disposés sur un support commun. Une variante de b) est le cas où l'éprouvette est placée sur la surface support de l'instrument. La dureté apparente peut également être mesurée sur des éprouvettes plates n'ayant pas les dimensions normales à l'aide des méthodes N, H, L et M. Les modes opératoires décrits ne peuvent pas convenir pour toutes les formes et les dimensions d'éprouvettes possibles, mais ils sont adaptés à quelques-uns des types les plus courants, par exemple aux joints toriques.
General Information
Relations
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 48-2
First edition
2018-08
Rubber, vulcanized or
thermoplastic — Determination of
hardness —
Part 2:
Hardness between 10 IRHD and 100
IRHD
Caoutchouc vulcanisé ou thermoplastique — Détermination de la
dureté —
Partie 2: Dureté comprise entre 10 DIDC et 100 DIDC
Reference number
©
ISO 2018
© ISO 2018
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2018 – All rights reserved
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 2
3 Terms and definitions . 2
4 Principle . 3
5 Apparatus . 3
5.1 General . 3
5.2 Methods N, H, L and M . 3
5.3 Methods CN, CH, CL and CM. 5
5.3.1 Cylindrical surfaces of radius greater than 50 mm . 5
5.3.2 Surfaces with double curvature of large radius greater than 50 mm . 5
5.3.3 Cylindrical surfaces of radius 4 mm to 50 mm or small test pieces with
double curvature . . 5
5.3.4 Small O-rings and articles of radius of curvature less than 4 mm . 5
6 Test pieces . 5
6.1 General . 5
6.2 Methods N, H, L and M . 5
6.2.1 General. 5
6.2.2 Thickness . 5
6.2.3 Lateral dimensions . . 6
6.3 Methods CN, CH, CL and CM. 6
7 Time interval between forming and testing . 7
8 Conditioning of test pieces . 7
9 Temperature of test . 7
10 Procedure. 7
11 Number of readings . 7
12 Expression of results . 8
13 Precision . 8
14 Test report .10
Annex A (informative) Empirical relationship between indentation and hardness .12
Annex B (informative) Precision results from interlaboratory test programmes .15
Bibliography .23
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: www .iso .org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products,
Subcommittee SC 2, Testing and analysis.
This first edition of ISO 48-2 cancels and replaces ISO 48:2010, of which it constitutes a minor revision.
The changes compared to the previous edition are as follows:
— a new standard number has been given.
— in the Introduction, an explanation of the purpose of the grouping work has been added.
— in Clause 12, an alternative way of expressing results has been added.
A list of all parts in the ISO 48 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
iv © ISO 2018 – All rights reserved
Introduction
ISO/TC 45/SC 2 established a principle that it would be helpful for users if standards on the same subject
but covering different aspects or methods were grouped together, preferably with an introductory
guidance standard, rather than being scattered throughout the numbering system. This has been
achieved for some subjects, for example curemeters (ISO 6502) and dynamic properties (ISO 4664).
In 2017, it was decided to group standards for hardness and, subsequently, it was agreed that they
would be grouped under the ISO 48 number. The new standards together with the previously numbered
standards are listed below.
— ISO 48-1: former ISO 18517
— ISO 48-2: former ISO 48
— ISO 48-3: former ISO 27588
— ISO 48-4: former ISO 7619-1
— ISO 48-5: former ISO 7619-2
— ISO 48-6: former ISO 7267-1
— ISO 48-7: former ISO 7267-2
— ISO 48-8: former ISO 7267-3
— ISO 48-9: former ISO 18898
The hardness test specified in this document is intended to provide a rapid measurement of rubber
stiffness, unlike hardness tests on other materials which measure resistance to permanent deformation.
Hardness is measured from the depth of indentation of a spherical indentor, under a specified force, into
a rubber test piece. An empirical relationship between depth of indentation and Young's modulus for a
perfectly elastic isotropic material has been used to derive a hardness scale which can conveniently be
used for most rubbers.
When it is required to determine the value of Young's modulus itself, it is expected that an appropriate
test method be used, for example that described in ISO 7743.
The guide to hardness testing, ISO 48-1, can also be a useful reference.
INTERNATIONAL STANDARD ISO 48-2:2018(E)
Rubber, vulcanized or thermoplastic — Determination of
hardness —
Part 2:
Hardness between 10 IRHD and 100 IRHD
WARNING 1 — Persons using this document should be familiar with normal laboratory practice.
This document does not purport to address all of the safety problems, if any, associated with its
use. It is the responsibility of the user to establish appropriate safety and health practices and to
determine the applicability of any other restrictions.
WARNING 2 — Certain procedures specified in this document might involve the use or generation
of substances, or the generation of waste, that could constitute a local environmental hazard.
Reference should be made to appropriate documentation on safe handling and disposal after use.
1 Scope
This document specifies four methods for the determination of the hardness of vulcanized or
thermoplastic rubbers on flat surfaces (standard-hardness methods) and four methods for the
determination of the apparent hardness of curved surfaces (apparent-hardness methods). The hardness
is expressed in international rubber hardness degrees (IRHD). The methods cover the hardness range
from 10 IRHD to 100 IRHD.
These methods differ primarily in the diameter of the indenting ball and the magnitude of the indenting
force, these being chosen to suit the particular application. The range of applicability of each method is
indicated in Figure 1.
This document does not specify a method for the determination of hardness by a pocket hardness
meter, which is described in ISO 48-5.
This document specifies the following four methods for the determination of standard hardness.
— Method N (normal test) is appropriate for rubbers with a hardness in the range 35 IRHD to 85 IRHD,
but can also be used for hardnesses in the range 30 IRHD to 95 IRHD.
— Method H (high-hardness test) is appropriate for rubbers with a hardness in the range 85 IRHD to
100 IRHD.
— Method L (low-hardness test) is appropriate for rubbers with a hardness in the range 10 IRHD to
35 IRHD.
— Method M (microtest) is essentially a scaled-down version of the normal test method N, permitting
the testing of thinner and smaller test pieces. It is appropriate for rubbers with a hardness in the
range 35 IRHD to 85 IRHD, but can also be used for hardnesses in the range 30 IRHD to 95 IRHD.
NOTE 1 The value of the hardness obtained by method N within the ranges 85 IRHD to 95 IRHD and 30 IRHD to
35 IRHD might not agree precisely with that obtained using method H or method L, respectively. The difference
is not normally significant for technical purposes.
NOTE 2 Because of various surface effects in the rubber and the possibility of slight surface roughness
(
...
NORME ISO
INTERNATIONALE 48-2
Première édition
2018-08
Caoutchouc vulcanisé ou
thermoplastique — Détermination de
la dureté —
Partie 2:
Dureté comprise entre 10 DIDC et
100 DIDC
Rubber, vulcanized or thermoplastic — Determination of hardness —
Part 2: Hardness between 10 IRHD and 100 IRHD
Numéro de référence
©
ISO 2018
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2018
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2018 – Tous droits réservés
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application . 1
2 Références normatives . 2
3 Termes et définitions . 3
4 Dureté de pénétration . 3
5 Appareillage . 4
5.1 Généralités . 4
5.2 Méthodes N, H, L et M . 4
5.3 Méthodes CN, CH, CL et CM . 5
6 Éprouvettes . 6
6.1 Généralités . 6
6.2 Méthodes N, H, L et M . 6
6.2.1 Généralités . 6
6.2.2 Épaisseur . 6
6.2.3 Dimensions latérales . 7
6.3 Méthodes CN, CH, CL et CM . 7
7 Délai entre vulcanisation et essai . 7
8 Conditionnement des éprouvettes . 8
9 Température d'essai . 8
10 Mode opératoire. 8
11 Nombre de lectures . 8
12 Expression des résultats. 9
13 Fidélité . 9
14 Rapport d'essai .11
Annexe A (informative) Relation empirique entre pénétration et dureté .12
Annexe B (informative) Résultats de fidélité provenant de programmes d'essais
interlaboratoires .15
Bibliographie .23
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l’élaboration du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de
brevets reçues par l’ISO (voir www .iso .org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion
de l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www .iso .org/avant -propos.
Le présent document a été élaboré par le comité technique ISO/TC 45, Élastomères et produits à base
d'élastomères, sous-comité SC 2, Essais et analyses.
Cette première édition de l'ISO 48-2 annule et remplace l’ISO 48:2010, dont il constitue une révision
mineure. Les modifications par rapport à la précédente édition sont les suivantes:
— une nouvelle référence a été donnée.
— dans l'Introduction, une explication de l'objet du travail de regroupement a été ajoutée.
— à l’Article 12, une autre façon d'exprimer les résultats a été ajoutée.
Une liste de toutes les parties de l'ISO 48 peut être trouvée sur le site internet de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www .iso .org/fr/members .html.
iv © ISO 2018 – Tous droits réservés
Introduction
L'ISO/TC 45/SC 2 a établi un principe selon lequel il serait utile pour les utilisateurs que les normes
portant sur la même thématique, mais couvrant différents aspects ou méthodes, soient regroupées
de préférence avec une norme de lignes directrices introductives, plutôt que dispersées dans tout le
système de numérotation. Cela a été réalisé pour certains sujets, par exemple les rhéomètres (ISO 6502)
et les propriétés dynamiques (ISO 4664).
En 2017, il a été décidé de regrouper les normes de dureté et, par la suite, il a été convenu qu'elles
seraient regroupées sous la référence ISO 48. Les nouvelles normes avec leurs anciennes références
sont listées ci-dessous.
— ISO 48-1: précédemment ISO 18517
— ISO 48-2: précédemment ISO 48
— ISO 48-3: précédemment ISO 27588
— ISO 48-4: précédemment ISO 7619-1
— ISO 48-5: précédemment ISO 7619-2
— ISO 48-6: précédemment ISO 7267-1
— ISO 48-7: précédemment ISO 7267-2
— ISO 48-8: précédemment ISO 7267-3
— ISO 48-9: précédemment ISO 18898
L'essai de dureté spécifié dans le présent document est destiné à permettre un mesurage rapide de
la raideur du caoutchouc, à la différence des essais de dureté effectués sur d'autres matériaux pour
mesurer la résistance à une déformation permanente.
La dureté est mesurée à partir de la profondeur de pénétration d'un pénétrateur sphérique, appliqué
avec une force spécifiée, sur une éprouvette en caoutchouc. Une relation empirique entre la profondeur
de pénétration et le module de Young, pour un matériau isotrope parfaitement élastique, a été utilisée
pour établir une échelle de dureté qui convient pour la plupart des caoutchoucs.
Lorsqu'il s'agit de déterminer la valeur du module de Young lui-même, il est préférable d'utiliser une
méthode d'essai appropriée, par exemple celle décrite dans l'ISO 7743.
Il est également possible de faire référence au guide relatif aux essais de dureté, l'ISO 48-1.
NORME INTERNATIONALE ISO 48-2:2018(F)
Caoutchouc vulcanisé ou thermoplastique —
Détermination de la dureté —
Partie 2:
Dureté comprise entre 10 DIDC et 100 DIDC
AVERTISSEMENT 1 — Il convient que l'utilisateur du présent document connaisse bien les
pratiques courantes de laboratoire. Le présent document n'a pas pour but de traiter tous les
problèmes de sécurité qui sont, le cas échéant, liés à son utilisation. Il incombe à l'utilisateur
d'établir des pratiques appropriées en matière d'hygiène et de sécurité, et de déterminer
l'applicabilité de toute autre restriction.
AVERTISSEMENT 2 — Certains modes opératoires spécifiés dans le présent document peuvent
impliquer l'utilisation ou la génération de substances, ou la génération de déchets, susceptibles
de constituer un danger environnemental localisé. Il convient de se référer à la documentation
appropriée relative à la manipulation et à l'élimination de ces substances en toute sécurité après
utilisation.
1 Domaine d'application
Le présent document spécifie quatre méthodes de détermination de la dureté des caoutchoucs vulcanisés
ou thermoplastiques sur des surfaces planes (méthodes de détermination de la dureté normale) et
quatre méthodes de détermination de la dureté apparente sur des surfaces courbes (méthodes de
détermination de la dureté apparente). La dureté est exprimée en degrés internationaux de dureté du
caoutchouc (DIDC). Les méthodes couvrent les duretés comprises entre 10 DIDC et 100 DIDC.
Les méthodes diffèrent principalement par le diamètre de la bille du pénétrateur et par la valeur
de la force de pénétration, celles-ci étant choisies en fonction de l'application considérée. La plage
d'applicabilité de chaque méthode est indiquée à la Figure 1.
Le présent document ne spécifie pas de méthode de détermination de la dureté à l'aide d'un duromètre
de poche, qui est décrite dans l'ISO 48-5.
Le présent document spécifie les quatre méthodes suivantes pour la détermination de la dureté
normale.
— La méthode N (essai normal) est appropriée pour les caoutchoucs dont la dureté est comprise entre
35 DIDC et 85 DIDC, mais elle peut également être utilisée pour ceux dont la dureté est comprise
entre 30 DIDC et 95 DIDC.
— La méthode H (essai pour dureté élevée) est appropriée pour les caoutchoucs dont la dureté est
comprise entre 85 DIDC et 100 DIDC.
— La méthode L (essai pour faible dureté) est appropriée pour les caoutchoucs dont la dureté est
compris
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.