ISO 19840:2012
(Main)Paints and varnishes — Corrosion protection of steel structures by protective paint systems — Measurement of, and acceptance criteria for, the thickness of dry films on rough surfaces
Paints and varnishes — Corrosion protection of steel structures by protective paint systems — Measurement of, and acceptance criteria for, the thickness of dry films on rough surfaces
ISO 19840:2012 specifies a procedure for the verification of dry-film thickness against nominal dry-film thickness on rough surfaces, including the adjustment of the instruments used, the definition of inspection areas, sampling plans, measurement methods and acceptance/rejection criteria. The procedure is based on the use of instruments of the permanent magnet, electromagnet and eddy current type. Instrument accuracy is verified both at zero and at a known thickness on a smooth surface and adjusted if necessary. It does not apply to nominal dry-film thicknesses less than 40 µm.
Peintures et vernis — Anticorrosion des structures en acier par systèmes de peinture — Mesure et critères d'acceptation de l'épaisseur d'un feuil sec sur des surfaces rugueuses
L'ISO 19840:2012 spécifie un mode opératoire de vérification de l'épaisseur d'un feuil sec par rapport à l'épaisseur nominale d'un feuil sec sur des surfaces rugueuses, y compris le réglage des instruments utilisés, la définition des aires de contrôle, des plans d'échantillonnage, des méthodes de mesure et des critères d'acceptation ou de refus. Le mode opératoire décrit est fondé sur l'utilisation d'instruments basés sur les principes de l'aimant permanent, de l'électro-aimant et du courant de Foucault. La précision de l'instrument est vérifiée à zéro et à une épaisseur connue sur une surface lisse et réglée si nécessaire. Il s'applique si l'épaisseur nominale du feuil sec est égale ou supérieure à 40 µm.
General Information
Relations
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 19840
Second edition
2012-09-01
Paints and varnishes — Corrosion
protection of steel structures by
protective paint systems — Measurement
of, and acceptance criteria for, the
thickness of dry films on rough surfaces
Peintures et vernis — Anticorrosion des structures en acier par
systèmes de peinture — Mesure et critères d’acceptation de l’épaisseur
d’un feuil sec sur des surfaces rugueuses
Reference number
©
ISO 2012
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO’s
member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2012 – All rights reserved
Contents Page
Foreword .iv
Introduction . v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Principle . 3
4.1 General . 3
4.2 Principle of the applicable measurement methods . 3
5 Apparatus and materials . 3
5.1 General . 3
5.2 Measurement equipment using a magnetic field . 4
5.3 Materials . 4
6 Procedure . 5
6.1 Sampling plan . 5
6.2 Adjustment of the instrument . 5
6.3 Measurement . 6
7 Correction values . 6
8 Expression of results . 7
9 Acceptance/rejection criteria . 7
10 Test report . 8
Annex A (informative) Method based on adjusting the instrument to known thicknesses on a
rough surface . 9
Annex B (informative) Multiple readings . 11
Annex C (informative) Areas requiring special consideration .12
Annex D (normative) Determination of a specific correction value .13
Annex E (informative) Example of a test report form.14
Bibliography .16
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International
Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 19840 was prepared by Technical Committee ISO/TC 35, Paints and varnishes, Subcommittee SC 14,
Protective paint systems for steel structures.
This second edition cancels and replaces the first edition (ISO 19840:2004), which has been technically and
editorially revised as follows:
a) the descriptions in 4.2 of the principle of the measurement methods have been improved;
b) a description of eddy current measurement equipment has been introduced (see 5.2.4);
c) Figure 1 has been made language-independent;
d) in line A8 in Annex E, the references to lines A7 and A8 have been corrected to A6 and A7;
e) in line B1 in Annex E, the reference to ISO 8503-1 has been corrected to “the relevant part of ISO 8501”;
f) a Bibliography has been added for the informative references ISO 8501-1 to ISO 8501-4.
iv © ISO 2012 – All rights reserved
Introduction
This International Standard supplements the ISO 12944 series with regard to the measurement and acceptance
criteria for the thickness of a dry film. If specified or agreed, the standard can also be used for other applications.
The objective of this International Standard is to achieve uniformity of practice for measuring the dry-film
thickness of a coating on a roughened surface. The chosen methods entail the measurement of dry-film
thickness using measurement instruments based on the permanent magnet principle and the inductive magnet
principle. Instruments using the eddy current principle can be used but their use is normally on non-ferrous
metal surfaces.
If a coating is applied to a roughened steel substrate, the measurement of its dry-film thickness is more
complicated than for smooth surfaces. Roughened steel substrates include those prepared by abrasive blast-
cleaning or abrading.
The effect of surface roughness on the measurement result increases with profile depth, but the result will also
depend on the design of the measurement probe and the thickness of the coating.
Annex A, which is informative, is a method based on adjusting the instrument to known thicknesses on a rough
surface. In this method, no correction value is used. In this standard, individual readings are used. Annex B
describes a method for multiple readings. The methods in Annexes A and B are intended to be used only if
specified or agreed.
INTERNATIONAL STANDARD ISO 19840:2012(E)
Paints and varnishes — Corrosion protection of steel structures
by protective paint systems — Measurement of, and acceptance
criteria for, the thickness of dry films on rough surfaces
1 Scope
This International Standard specifies a procedure for the verification of dry-film thickness against nominal dry-
film thickness on rough surfaces, including the adjustment of the instruments used, the definition of inspection
areas, sampling plans, measurement methods and acceptance/rejection criteria.
For the purposes of this standard, any specified thickness is taken to be nominal as defined in ISO 12944-5,
and the dry-film thickness is the typical thickness above the peaks of the surface profile.
The procedure described in this International Standard is based on the use of instruments of the permanent
magnet, electromagnet and eddy current type. Instrument accuracy is verified both at zero and at a known
thickness on a smooth surface and adjusted if necessary.
Measurements taken on a coating on a roughened steel substrate will therefore be higher than the actual value
above the peaks of the profile. The thickness of the dry film above the peaks of the profile is defined as the
instrument reading minus an appropriate correction value.
The dry-film thickness is obtained by using the appropriate correction value applied to readings based on
adjustment on a smooth, flat steel surface.
Where individual readings, based on adjustment on a smooth, flat steel surface without the use of correction
values, are specified or agreed, it is important to recognize that this method does not conform with this
International Standard.
This standard is applicable if the nominal dry-film thickness is 40 µm or greater.
NOTE If the nominal thickness is less than the surface roughness of the substrate, the uncertainty of the measurement
will increase.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced document
(including any amendments) applies.
ISO 2808, Paints and varnishes — Determination of film thickness
ISO 8503-1, Preparation of steel substrates before application of paints and related products — Surface
roughness characteristics of blast-cleaned steel substrates — Part 1: Specifications and definitions for ISO
surface profile comparators for the assessment of abrasive blast-cleaned surfaces
ISO 12944-1, Paints and varnishes — Corrosion protection of steel structures by protective paint systems —
Part 1: General introduction
ISO 12944-2, Paints and varnishes — Corrosion protection of steel structures by protective paint systems —
Part 2: Classification of environments
ISO 12944-3, Paints and varnishes — Corrosion protection of steel structures by protective paint systems —
Part 3: Design considerations
ISO 12944-4, Paints and varnishes — Corrosion protection of steel structures by protective paint systems —
Part 4: Types of surface and surface preparation
ISO 12944-5, Paints and varnishes — Corrosion protection of steel structures by protective paint systems —
Part 5: Protective paint systems
ISO 12944-6, Paints and varnishes — Corrosion protection of steel structures by protective paint systems —
Part 6: Laboratory performance test methods
ISO 12944-7, Paints and varnishes — Corrosion protection of steel structures by protective paint systems —
Part 7: Execution and supervision of paint work
ISO 12944-8, Paints and varnishes — Corrosion protection of steel structures by protective paint systems —
Part 8: Development of specifications for new work and maintenance
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
3.1
dry-film thickness
DFT
thickness of a coating remaining over the peaks of a rough surface when the coating has hardened
3.2
individual reading
figure displayed by the film thickness instrument
3.3
correction value
allowance for the influence of the abrasive blast-cleaned or otherwise roughened surface on the reading of the
film thickness instrument
3.4
individual dry-film thickness
individual reading minus a correction value
3.5
mean dry-film thickness
arithmetic mean of all the individual dry-film thicknesses in the inspection area
3.6
nominal dry-film thickness
NDFT
dry-film thickness specified for each coat or for the whole paint system to achieve the required durability
3.7
inspection area
designated area for which a sampling plan is established and which can be the whole structure or sections of
the whole structure
3.8
sampling plan
plan which defines the number of measurements to be taken on an inspection area
3.9
adjustment
process of aligning the readings of a dry-film thickness gauge to known thickness values in order to improve
the accuracy of the gauge on a specific surface or within a specific portion of its measurement range
2 © ISO 2012 – All rights reserved
3.10
surface profile
micro-roughness of a surface
NOTE This is generally expressed as the height of the major peaks relative to the major valleys.
[ISO 8503-1:2012]
3.11
maximum dry-film thickness
highest acceptable dry-film thickness above which the performance of the paint or the paint system might be impaired
4 Principle
4.1 G
...
NORME ISO
INTERNATIONALE 19840
Deuxième édition
2012-09-01
Peintures et vernis — Anticorrosion
des structures en acier par systèmes
de peinture — Mesure et critères
d’acceptation de l’épaisseur d’un feuil
sec sur des surfaces rugueuses
Paints and varnishes — Corrosion protection of steel structures by
protective paint systems — Measurement of, and acceptance criteria
for, the thickness of dry films on rough surfaces
Numéro de référence
©
ISO 2012
DOCUMENT PROTÉGÉ PAR COPYRIGHT
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l’accord écrit
de l’ISO à l’adresse ci-après ou du comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Publié en Suisse
ii © ISO 2012 – Tous droits réservés
Sommaire Page
Avant-propos .iv
Introduction . v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 2
4 Principe . 3
4.1 Généralités . 3
4.2 Principe des méthodes de mesure applicables . 3
5 Appareillage et matériel . 4
5.1 Généralités . 4
5.2 Équipements de mesure utilisant un champ magnétique . 4
5.3 Matériel . 4
6 Mode opératoire . 5
6.1 Plan d’échantillonnage . 5
6.2 Réglage de l’instrument . 5
6.3 Mesures . 6
7 Valeurs de correction . 6
8 Expression des résultats . 7
9 Critères d’acceptation et de refus . 7
10 Rapport d’essai . 8
Annexe A (informative) Méthode basée sur le réglage de l’instrument à des épaisseurs connues sur une
surface rugueuse . 9
Annexe B (informative) Lectures multiples . 11
Annexe C (informative) Aires nécessitant une attention particulière .12
Annexe D (normative) Détermination d’une valeur spécifique de correction .13
Annexe E (informative) Exemple de formulaire de rapport d’essai .14
Bibliographie .16
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux de
normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général confiée aux
comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales,
en liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec la Commission
électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI, Partie 2.
La tâche principale des comités techniques est d’élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur publication
comme Normes internationales requiert l’approbation de 75 % au moins des comités membres votants.
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de droits
de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable de ne pas avoir
identifié de tels droits de propriété et averti de leur existence.
L’ISO 19840 a été élaborée par le comité technique ISO/TC 35, Peintures et vernis, sous-comité SC 14,
Systèmes de peinture protectrice pour les structures en acier.
Cette deuxième édition annule et remplace la première édition (ISO 19840:2004), qui a fait l’objet d’une révision
technique et rédactionnelle, comme suit:
a) les descriptions du principe des méthodes de mesure en 4.2 ont été améliorées;
b) une description de l’équipement de mesure du courant de Foucault a été introduite (voir 5.2.4);
c) la Figure 1 a été rendue indépendante de la langue;
d) à la ligne A8 de l’Annexe E, les références aux lignes A7 et A8 ont été corrigées en A6 et A7;
e) à la ligne B1 de l’Annexe E, la référence à l’ISO 8503-1 a été corrigée en «la partie pertinente de l’ISO 8501»;
f) une Bibliographie a été ajoutée pour les références informatives ISO 8501-1 à ISO 8501-4.
iv © ISO 2012 – Tous droits réservés
Introduction
La présente Norme internationale traite, en complément de la série ISO 12944, de la mesure et des critères
d’acceptation de l’épaisseur d’un feuil sec. Si cela est spécifié ou convenu, la norme peut également servir à
d’autres applications.
La présente Norme internationale a pour objet de définir une pratique uniforme de mesure de l’épaisseur
du feuil sec d’un revêtement sur une surface rugueuse. Les méthodes choisies utilisent des instruments de
mesure basés sur les principes de l’aimant permanent et de l’aimant inductif. Des instruments basés sur le
principe du courant de Foucault peuvent être utilisés, bien qu’ils s’appliquent normalement aux surfaces en
métaux non ferreux.
La mesure de l’épaisseur d’un feuil sec est plus complexe sur un subjectile d’acier rugueux que sur une surface
lisse. Les subjectiles d’acier rugueux incluent ceux préparés par décapage à l’abrasif ou par abrasion.
L’incidence de la rugosité de surface sur la mesure est d’autant plus importante que la profondeur de profil
augmente, mais elle est aussi liée à la conception de la sonde de mesure et à l’épaisseur du revêtement.
L’Annexe A, informative, décrit une méthode consistant à régler l’instrument à une épaisseur connue sur une
surface rugueuse. Cette méthode n’utilise pas de valeur de correction. La présente Norme internationale utilise
des lectures individuelles. L’Annexe B décrit une méthode de lectures multiples. Les méthodes décrites aux
Annexes A et B ne sont destinées à être utilisées que si cela est spécifié ou convenu.
NORME INTERNATIONALE ISO 19840:2012(F)
Peintures et vernis — Anticorrosion des structures en acier par
systèmes de peinture — Mesure et critères d’acceptation de
l’épaisseur d’un feuil sec sur des surfaces rugueuses
1 Domaine d’application
La présente Norme internationale spécifie un mode opératoire de vérification de l’épaisseur d’un feuil sec par
rapport à l’épaisseur nominale d’un feuil sec sur des surfaces rugueuses, y compris le réglage des instruments
utilisés, la définition des aires de contrôle, des plans d’échantillonnage, des méthodes de mesure et des
critères d’acceptation ou de refus.
Pour les besoins de la présente Norme internationale, toute épaisseur spécifiée est une valeur nominale selon la
définition de l’ISO 12944-5 et l’épaisseur du feuil sec est l’épaisseur type au-dessus des pics du profil de surface.
Le mode opératoire décrit dans la présente Norme internationale est fondé sur l’utilisation d’instruments
basés sur les principes de l’aimant permanent, de l’électro-aimant et du courant de Foucault. La précision de
l’instrument est vérifiée à zéro et à une épaisseur connue sur une surface lisse et réglée si nécessaire.
Les mesures prises d’un revêtement sur un subjectile d’acier rugueux seront par conséquent plus élevées que
la valeur réelle au-dessus des pics du profil de surface. L’épaisseur du feuil sec au-dessus des pics du profil
est définie comme étant égale à la valeur lue sur l’instrument, moins une valeur de correction donnée.
Pour obtenir l’épaisseur du feuil sec, on applique une valeur de correction aux lectures correspondant à un
réglage de l’instrument de mesure sur une surface d’acier plate et lisse.
S’il est spécifié ou convenu que les lectures individuelles utilisent un réglage de l’instrument sur surface d’acier
lisse sans valeur de correction, il est important de souligner que cette méthode n’est pas conforme à la présente
Norme internationale.
La présente Norme internationale s’applique si l’épaisseur nominale du feuil sec est égale ou supérieure à 40 µm.
NOTE Si l’épaisseur nominale est inférieure à la rugosité de surface du subjectile, l’incertitude de la mesure augmente.
2 Références normatives
Les documents de référence suivants sont indispensables pour l’application du présent document. Pour les
références datées, seule l’édition citée s’applique. Pour les références non datées, la dernière édition du
document de référence s’applique (y compris les éventuels amendements).
ISO 2808, Peintures et vernis — Détermination de l’épaisseur du feuil
ISO 8503-1, Préparation des subjectiles d’acier avant application de peintures et de produits assimilés —
Caractéristiques de rugosité des subjectiles d’acier décapés — Partie 1: Spécifications et définitions des
comparateurs viso-tactiles ISO pour caractériser les surfaces décapées par projection d’abrasif
ISO 12944-1, Peintures et vernis — Anticorrosion des structures en acier par systèmes de peinture — Partie 1:
Introduction générale
ISO 12944-2, Peintures et vernis — Anticorrosion des structures en acier par systèmes de peinture — Partie 2:
Classification des environnements
ISO 12944-3, Peintures et vernis — Anticorrosion des structures en acier par systèmes de peinture — Partie 3:
Conception et dispositions constructives
ISO 12944-4, Peintures et vernis — Anticorrosion des structures en acier par systèmes de peinture — Partie 4:
Types de surface et préparation de surface
SO 12944-5, Peintures et vernis — Anticorrosion des structures en acier par systèmes de peinture — Partie 5:
Systèmes de peinture
ISO 12944-6, Peintures et vernis — Anticorrosion des structures en acier par systèmes de peinture — Partie 6:
Essais de performance en laboratoire
ISO 12944-7, Peintures et vernis — Anticorrosion des structures en acier par systèmes de peinture — Partie 7:
Exécution et surveillance des travaux de peinture
ISO 12944-8, Peintures et vernis — Anticorrosion des structures en acier par systèmes de peinture — Partie 8:
Développement de spécifications pour les travaux neufs et l’entretien
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s’appliquent.
3.1
épaisseur de feuil sec
DFT
épaisseur d’un revêtement restant au-dessus des pics d’une surface rugueuse après durcissement du revêtement
3.2
lecture individuelle
chiffre affiché par l’instrument de mesure de l’épaisseur de feuil
3.3
valeur de correction
valeur permettant de prendre en compte l’influence de la surface rugueuse décapée par projection d’abrasif ou
dépoli selon une autre technique sur la lecture de l’instrument de mesure de l’épaisseur de feuil
3.4
épaisseur individuelle du feuil sec
lecture individuelle moins une valeur de correction
3.5
épaisseur moyenne du feuil sec
moyenne arithmétique de toutes les épaisseurs individuelles du feuil sec dans l’aire de contrôle
3.6
épaisseur nominale du feuil sec
NDFT
épaisseur du feuil sec spécifiée pour chaque couche ou pour l’ensemble du système de peinture afin d’obtenir
la durabilité requise
3.7
aire de contrôle
aire désignée sur laquelle un plan d’échantillonnage est établi et qui peut couvrir l’ensemble ou une partie
de la structure
3.8
plan d’échantillon
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.